以含有4个环氧官能团的TGDDM环氧树脂与ECC环氧树脂混合为基体树脂体系，通过配方设计，加入固化剂和固化促进剂，制得缩水甘油胺型环氧体系粘合剂，并对其性能进行了研究。结果表明：4种配方体系具有优异的综合性能，具有较低的吸水率和良好的疏水性能，随着配方中TGDDM的比例增大，体系的粘度随之增大；随着配方中ECC含量的增加，试样的拉伸剪切强度变大，其中PF3和PF4两个体系的最大剪切强度超过20 MPa。
Using the mixture of TGDDM epoxy resin which has four epoxy groups and ECC epoxy res-in as matrix resin, a glycidyl amine type epoxy resin adhesive was prepared by formula design and add-ing curing agent and curing accelerator, and its properties were studied. The results show that four kinds of formula system have excellent comprehensive properties and lower water absorption. With the increase of TGDDM ratio, the viscosity of the system increases. With the increase of ECC content, the tensile shear strength increases, and the tensile shear strength maximum of the PF3 and PF4 systems is more than 20MPa.
参考文献
| [1] | 赵春玲,寇开昌,张教强,晁敏,王志超.特种胶粘剂的研究进展[J].中国胶粘剂,2009(03):48-55. |
| [2] | 胡忠杰,虞鑫海,徐永芬,赵炯心,傅菊荪.四缩水甘油基-4,4,-二氨基二苯甲烷/1,4-双（4-氨基苯氧基）苯环氧树脂体系固化反应的动力学模型[J].绝缘材料,2007(06):50-52. |
| [3] | 胡孝勇,袁晓玲.耐高温环氧树脂胶黏剂研究进展[J].化学与黏合,2009(05):49-52. |
| [4] | 孙振华,罗辉阳,赵世琦.橡胶增韧环氧树脂的增韧力学模型综述[J].高分子材料科学与工程,2001(02):1-4. |
| [5] | 徐永芬,虞鑫海,赵炯心,傅菊蓀.多官能环氧树脂/2,2,-双（3-氨基-4-羟基苯基）六氟丙烷体系的固化反应动力学研究[J].绝缘材料,2007(04):42-44. |
| [6] | 费斐,虞鑫海.TGDDM环氧树脂的研究进展[J].粘接,2009(09):68-72. |
| [7] | 徐永芬,虞鑫海,赵炯心,傅菊荪.TGDDM/3,3'-二氨基-4,4'-二羟基联苯固化反应动力学研究[J].绝缘材料,2010(05):57-60. |
| [8] | 秦传香.聚酰亚胺用于耐高温环氧胶粘剂体系研究进展[J].合成技术及应用,2001(04):22-26. |
| [9] | Premkumar S;Chozhan CK;Alagar M .Studies on thermal, mechanical and morphological behaviour of caprolactam blocked methylenediphenyl diisocyanate toughened bismaleimide modified epoxy matrices[J].European Polymer Journal,2008(8):2599-2607. |
| [10] | 王超;张斌;李奇力 等.耐高温环氧树脂粘胶剂的研制[J].中国粘胶剂,1999,8(03):12-13. |
| [11] | 陈平;刘胜平.环氧树脂[M].北京:化学工业出版社,2000 |
| [12] | 李旭日,陆波.环氧树脂胶粘剂的增韧填充改性[J].辽宁化工,2006(08):449-450,453. |
| [13] | 虞鑫海;赵炯心;徐永芬 等.一种含酚羟基聚酰亚胺粉末的制备方法[P].中国,1927908A,2007-03-14. |
| [14] | Su CC.;Woo EM. .CURE KINETICS AND MORPHOLOGY OF AMINE-CURED TETRAGLYCIDYL-4,4'-DIAMINODIPHENYLMETHANE EPOXY BLENDS WITH POLY(ETHER IMIDE)[J].Polymer: The International Journal for the Science and Technology of Polymers,1995(15):2883-2894. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%