In the strengthened layer of stainless steel after shot peening,there are a great amount of deformation microtwins which may act as structural strengthening factor and prevent the gradual relaxation of surface residual stress during fatigue,so as to keep its rather high level of bending fatigue strength.However,in the strengthened surface layer of low carbon steel, dislocation cell structure is so unstalbe during fatigue that its surface residual stress relaxation cannot be retarded.Therefore,the bending fatigue strength of the low carbon steel can not be improred by shot peening.