采用元素分析、X射线衍射和穆斯堡尔谱等手段研究了喷雾干燥沉淀Fe-Cu-K/SiO2催化剂在F-T合成反应过程中的物相变化. 结果表明,新鲜催化剂样品主要由α-Fe2O3组成,且81.1%的α-Fe2O3粒径小于13.5 nm. 随着反应时间的延长,催化剂表面碳沉积物的含量逐渐增多,不饱和度逐渐增大; χ-Fe5C2的含量逐渐增多,Fe3O4的含量逐渐减少并趋于稳定. 超顺磁Fe3+的含量呈先增加后减少的变化趋势. 由于碳沉积物是由CO生成的,而χ-Fe5C2是由α-Fe2O3经Fe3O4生成的,故催化剂表面碳沉积物的生成先于χ-Fe5C2的生成.
参考文献
| [1] | Yang J;Liu Y;Chang J;Wang Y N Bai L Xu Y Y Xiang H W Li Y W Zhong B .[J].Industrial and Engineering Chemistry Research,2003,42(21):5066. |
| [2] | 高海燕,杨文书,相宏伟,李永旺,孙予罕,刘涛,谢亚宁,张静,胡天斗.pH值对Co/SiO2催化剂还原性能的影响[J].催化学报,2002(05):430-434. |
| [3] | 杨骏,刘颖,李苑,张渊明,白亮,相宏伟,李永旺,钟炳.Fe-Mn催化剂对F-T合成反应的催化性能Ⅱ. 中后期反应性能[J].催化学报,2003(05):343-349. |
| [4] | Liu Z T;Li Y W;Zhou J L;Zhang Z X Zhang B J .[J].Applied Catalysis A:General,1997,161(1/2):137. |
| [5] | Wang Y N;Ma W P;Lu Y J;Yang J Xu Y Y Xiang H W Li Y W Zhao Y L Zhang B .[J].Journal of Fuel,2003,82(02):195. |
| [6] | Bai L;Xiang H W;Li Y W;Han Y Z, Zhong B .[J].FUEL,2002,81(11/12):1577. |
| [7] | Mansker L D;Jin Y M;Bukur D B;Datye A K .[J].Applied Catalysis A:General,1999,186(1/2):277. |
| [8] | Reymond J P;Meriaudeau P;Pommier B;Bennett C O .[J].Journal of Catalysis,1980,64(01):163. |
| [9] | Bukur DB.;Rosynek MP.;Li CP.;Wang DJ.;Rao KRPM.;Huffman GP.;Okabe K. .ACTIVATION STUDIES WITH A PRECIPITATED IRON CATALYST FOR FISCHER-TROPSCH SYNTHESIS .1. CHARACTERIZATION STUDIES[J].Journal of Catalysis,1995(2):353-365. |
| [10] | Dictor R A;Bell A T .[J].Journal of Catalysis,1986,97(02):121. |
| [11] | Jaggi N K;Schwartz L H;Butti J B;Papp H Baerns M .[J].Applied Catalysis,1985,13(02):347. |
| [12] | 黄止而;曾贻伟;李哲;张志新,王定珠 .[J].燃料化学学报,1991,19(01):35. |
| [13] | 刘昭铁;周敬来;张碧江 .[J].石油化工高等学校学报,1995,8(01):14. |
| [14] | 刘昭铁 .[D].太原:中国科学院山西煤炭化学研究所,1994. |
| [15] | Zhao R;Sudsakorn K;Goodwin J G;Jothimurugesan K,Gangwal S K,Spivey J J .[J].Catalysis Today,2002,71(3/4):319. |
| [16] | Pham HN.;Gormley RJ.;Datye AK.;Viergutz A. .Improving the attrition resistance of slurry phase heterogeneous catalysts[J].Powder Technology,2000(3):196-203. |
| [17] | 张志新;唐曙光;周敬来 .[J].天然气化工,1992,17(02):7. |
| [18] | Lox E S;Marin G B;De Grave E;Bussiere P .[J].Applied Catalysis,1988,40(1/2):197. |
| [19] | Dwyer D J;Somorjai G A .[J].Journal of Catalysis,1978,52(02):291. |
| [20] | Rao V U S;Stiegel G J;Cinquegrane G J;Srivastava R D .[J].Fuel Processing Technology,1992,30(01):83. |
| [21] | Dry M E .[J].Catalysis Letters,1991,7(1-4):241. |
| [22] | van den Berg F R;Craje M W J;van der Kraan A M;Geus J W .[J].Applied Catalysis A:General,2003,242(02):403. |
| [23] | Motjope T R;Dlamini H T;Hearne G R;Coville N J .[J].Catalysis Today,2002,71(3/4):335. |
| [24] | Kündig W;Bommel H .[J].Physical Review,1966,142(02):327. |
| [25] | Jin Y;Datye A K .[J].Journal of Catalysis,2000,196(01):8. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%