针对酚醛泡沫脆性大、强度低等缺点,采用3种不同增强形式的玻璃纤维增强体,即短切玻璃纤维(SGF)、酚醛树脂浸渍固化的玻璃纤维针(GFN)及三维间隔连体织物,对酚醛泡沫进行增强.研究了纤维含量和纤维长度对酚醛泡沫压缩性能的影响规律,对比了不同增强形式纤维增强酚醛泡沫复合材料的压缩性能与保温性能.结果表明:当SGF长度为3 mm,与基体质量比为5％时,SGF增强酚醛泡沫的比压缩强度最佳,较纯泡沫的提高了21％;GFN(长度5 mm,与基体质量比为25％)增强酚醛泡沫的比强度提高8％;三维间隔连体织物增强酚醛泡沫的比强度虽略有下降,但其压缩强度(0.239 MPa)达到了承重类酚醛泡沫的要求.SGF和GFN增强的酚醛泡沫的热导率与纯酚醛泡沫的相比略有上升,但仍符合高效保温材料的要求;三维间隔连体织物增强酚醛泡沫的热导率上升明显.
参考文献
| [1] | 李珠;张泽平;刘元珍.建筑节能的重要性及一项新技术[J].工程力学,200623(02):141-149. |
| [2] | (O)nüt S;Soner S.Energy efficiency assessment for the antalya region hotels in Turkey[J].Energy and Buildings,200638(08):964-971. |
| [3] | Auad M L;Zhao L H;Shen H B.Flammability properties and mechanical performance of epoxy modified phenolic foams[J].Journal of Applied Polymer Science,2007104(03):1399-1407. |
| [4] | Shen H B;Lavoie A J;Nutt S R.Enhanced peel resistance of fiber reinforced phenolic foams[J].Composites Part A:Applied Science and Manufacturing,200334(10):941-948. |
| [5] | Shen H B .Toughening of phenolic foam[D].California:University of Southern California,2003. |
| [6] | Shen H B;Nutt S.Mechanical characterization of short fiber reinforced phenolic foam[J].Composites Part A:Applied Science and Manufacturing,200334(09):899-906. |
| [7] | Desai A;Auad M L;Shen H B.Mechanical behavior of hybrid composite phenolic foam[J].Journal of Cellular Plastics,200844(01):15-36. |
| [8] | 高爱君;李敏;王绍凯.三维间隔连体织物复合材料力学性能[J].复合材料学报,200825(02):87-93. |
| [9] | GB/T 8813-2008.硬质泡沫塑料压缩性能的测定[S].北京:中国标准出版社,2008. |
| [10] | GB/T 10294-2008.绝热材料稳态热阻及有关特性的测定-防护热板法[S].北京:中国标准出版社,2008. |
| [11] | Gibson L J;Ashby M F.Cellular solids:structure and prop erties[M].Cambridge:Cambridge University Press,1999:175-178. |
| [12] | 卢子兴;邹波.短纤维增强泡沫塑料力学行为的研究进展[J].复合材料学报,200522(05):1-8. |
| [13] | 王建华;芦艾;周秋明.短切玻璃纤维增强硬质聚氨酯泡沫塑料的压缩性能[J].高分子材料科学与工程,200117(03):150-152. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%