采用失重法研究了二氧化碳腐蚀环境中碳钢/不锈钢(N80/S31803)电偶对在高温高压下的电偶腐蚀行为,探讨了温度、压力及面积比对电偶腐蚀的影响.结果表明:常压下,随着温度的升高,CO2腐蚀环境中电偶对阳极(N80钢)的腐蚀速率有一个极大值;腐蚀速率的对数值与面积比的对数值呈线性关系.CO2分压为2.5 MPa、阴阳极面积比≤4时,电偶对阳极(N80钢)的腐蚀速率在不同温度下分别存在一个极大值和一个极小值;腐蚀速率都随着面积比的增大而增大.
参考文献
| [1] | M.E. El-Dahshan;A.M. Shams El Din;H.H. Haggag .Galvanic corrosion in the systems titanium/316 L stainless steel/Al brass in Arabian Gulf water[J].Desalination: The International Journal on the Science and Technology of Desalting and Water Purification,2002(2):161-169. |
| [2] | Zahran R R;Sedahmed G H .Galvanic corrosion of zinc in turbulentiy moving containing drag reducing polymers[J].Materials Letters,1997,31(05):29-33. |
| [3] | Semion C J .Lead/carbon steel galvanic corrosion evaluation[J].Journal of Nuclear Materials,1996,238:198-204. |
| [4] | 刘双梅,刘道新,樊国福.TA7钛合金/耐热不锈钢电偶腐蚀敏感性研究[J].材料工程,2000(01):17-19,30. |
| [5] | Abreu C M;Cristo'bal M J;Montemor M F .Galvanic cou-pling between carbon steel and anstenitic stainless steel in alkaline media[J].Eleetrochimiea Aeta,2002,47:2271-2279. |
| [6] | 张学元.二氧化碳腐蚀与控制[M].北京:化学工业出版社,2000:19-58. |
| [7] | 黄永昌.金属腐蚀与防护原理[M].上海:上海交通大学出版社,1989:76-83. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%