氯离子扩散系数和碳化速率是表征混凝土耐久性的主要指标.通过氯盐浸泡和快速碳化试验,基于试验检测和数据分析,研究了水灰比对氯离子扩散系数和碳化速率系数的影响规律.试验结果表明,水灰比越大,氯离子扩散系数越大,但水灰比过小时水灰比对扩散系数的影响程度降低；水灰比越大,混凝土碳化速度越快.碳化速率系数与水灰比成线性关系.结合试验数据并通过现有模型对比分析,给出较为合理的粉煤灰影响系数表达式和建议取值.
参考文献
| [1] | 金伟良;赵羽习.混凝土结构耐久性[M].北京:北京科学技术出版社,2002 |
| [2] | 牛荻涛.混凝土结构耐久性与寿命预测[M].北京:科学出版社,2003 |
| [3] | 孙伟;余洪发.混凝土结构工程的耐久性与寿命研究进展,土建结构工程的安全性与耐久性[M].北京:中国建筑工业出版社,2001 |
| [4] | LIFECON .Service Life Models:Instructions on methodology and application of models for the prediction of the residual service life for classified environmental loads and types of structures in Europe[D].Life Cycle Management of Conerete Infrastruetures for Improved Sustainability,2003. |
| [5] | Thomas M D A;Bentz E C.Life-365 computer program for predieting the service life and life-eyele costs of reinforced concrete exposed to chlorides[M].,2000 |
| [6] | 吴中伟;廉慧珍.高性能混凝土[M].北京:中国铁道出版社,1999 |
| [7] | Skijolsvold O.ACISP-91 Madrid Proc[M].,1986 |
| [8] | Ho D W S;Lewis R K.Carbonation of concrete and its predietion[J].Cement and Concrete Research,1987(17):489-504. |
| [9] | 方景;梅国兴;陆采荣.影响混凝土碳化主要因素及钢锈因素试验研究[J].混凝土,1993(02):35-43. |
| [10] | 蒋利学.混凝土碳化深度的计算与试验研究[J].混凝土,1996(04):12-16. |
| [11] | 朱安民.混凝士碳化与钢筋混凝土耐久性[J].混凝土,1992(06):18-22. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%