以纳米氧化铝粉和微米C粉为原料,通过碳热还原法合成AlON粉体,经无压烧结制备了AlON透明陶瓷,并对其微观组织、力学、热学和光学等性能进行了表征.结果表明:1875℃×24 h条件下无压烧结制备了平均晶粒尺寸为110 ～120 μm的AlON透明陶瓷,其室温抗弯强度为(275±25) MPa,室温比热容和导热系数分别为0.781 J/(g·K)和12.3 W/(m·K),该样品(1 mm厚)在1000 ～ 5000 nm波长范围内的直线透过率在80％左右,在3.93μm波长处光学透过率最高可达83.7％.
参考文献
| [1] | James W. McCauley;Parimal Patel;Mingwei Chen .AlON: A brief history of its emergence and evolution[J].Journal of the European Ceramic Society,2009(2):223-236. |
| [2] | XJ. Liu;F. Chen;F. Zhang .Hard transparent AlON ceramic for visible/IR windows[J].International Journal of Refractory Metals & Hard Materials,2013(Jul.):38-43. |
| [3] | 李跃龙,黎建明,苏小平,杨海,那木吉拉图,李楠,杨鹏,李金权.红外窗口和整流罩材料研究现状与发展趋势[J].人工晶体学报,2007(04):877-884. |
| [4] | 田庭燕,杜洪兵,姜华伟,孙峰,陈广乐,张微,吕科,彭珍珍.AlON透明陶瓷的制备与性能[J].硅酸盐学报,2010(08):1455-1458. |
| [5] | Xihai Jin;Lian Gao;Jing Sun .Highly Transparent AlON Pressurelessly Sintered from Powder Synthesized by a Novel Carbothermal Nitridation Method[J].Journal of the American Ceramic Society,2012(9):2801-2807. |
| [6] | 刘学建,袁贤阳,张芳,黄政仁,王士维.碳热还原氮化工艺制备AlON透明陶瓷[J].无机材料学报,2010(07):678-682. |
| [7] | Filiz Cinar Sahin;Halide Esra Kanbur;Burcu Apak .Preparation of AlON ceramics via reactive spark plasma sintering[J].Journal of the European Ceramic Society,2012(4):925-929. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%