用溶胶-凝胶(so-lgel)法制备了多铁Bi1-xLaxMnO3(BLMO,0.1≤x≤0.4)系列样品.样品的结构表征(X-射线衍射,扫描电子显微镜)及差热-热重(TG-DTA)分析测量显示,形成稳定的BLMO钙钛矿相的烧结温度位于900-950℃.La掺杂对BLMO样品(950℃烧结)的结构和磁性能的影响也被仔细研究.结果显示,随着La掺杂减少,样品中BLMO钙钛矿相减弱,铁磁转变温度(TC)由53K降至41K,而饱和磁化强度经历了先降低再升高的变化.这可归因于La含量较少的样品中Bi空位浓度的增加诱导了Mn-O-Mn键角的减小和局域Mn4+离子的增多,使得Mn3+和Mn4+离子的铁磁超交换增强和Mn3+离子的dz2轨道有序受到局域破坏.

Multiferroic Bi1-xLaxMnO3(BLMO,0.1(x≤0.4) samples were synthesized by the sol-gel method.The structure of BLMO samples were characterized by using X-ray diffraction(XRD),scanning electronic microscope(SEM),and the thermo gravimetric analysis-differential thermal analyses(TG-DTA).It was shown that the BLMO sample with a stable perovskite phase was sintered at temperature of 900-950℃.It was also carefully investigated that the La doping effect on the structural and magnetic properties of the BLMO samples sintered at 950℃.Our results indicated that the perovskite phase of samples was weakened as La doping reducing,the Curie temperature TC decrease from 53K to 41K,corresponding to the saturation magnetization experienced a lowering and then an enhancing.It was ascribed to the increase of Bi vacancies in La doping reducing samples,which induced a decrease of Mn-O-Mn bond angle and an increase of Mn4+ ions.This resulted in an enhancing of the ferromagnetic superexchange between Mn3+ and Mn4+ ions and a disrupting of the dz2 orbital ordering around the Mn3+ matrix.

参考文献

[1] 王克锋,刘俊明,王雨.单相多铁性材料--极化和磁性序参量的耦合与调控[J].科学通报,2008(10):1098-1135.
[2] I. O. Troyanchuk;O. S. Mantytskaja;H. Szymczak;M. Yu. Shvedun .Magnetic phase transitions in the system La{sub}(1-x)Bi{sub}xMnO{sub}(3+λ)[J].Low temperature physics: Simultaneous Russian - English publication,2002(7):569-573.
[3] Y. P. Wang;L. Zhou;M. F. Zhang;X. Y. Chen;J.-M. Liu;Z. G. Liu .Room-temperature saturated ferroelectric polarization in BiFeO_(3) ceramics synthesized by rapid liquid phase sintering[J].Applied physics letters,2004(10):1731-1733.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%