主要研究高强韧稀土镁合金筋板类构件等温精锻工艺及随后的锻件微观组织与性能的控制.通过Deform软件对典型筋板类构件的等温精锻工艺进行模拟研究,通过分析等温精锻工艺过程中金属材料的流动趋势及可能出现的问题,提出相应的解决方案,在随后的实验过程中,成功成形出具有高筋薄腹板的典型筋板类锻件.研究结果表明:筋板类构件等温精锻过程中在两个侧筋相交的位置充填最为困难,利用有限元方法对坯料尺寸进行优化设计,有效地改善了金属在复杂模具型腔内的充填能力,并降低了等温成形载荷,成形出表面质量良好的稀土镁合金精锻件.通过200℃时效63 h后,高强韧稀土镁合金筋板类构件的强度达到峰值,其峰值抗拉、屈服强度和延伸率分别为371、243 MPa和4.07％.β'相和长周期相在基体上的弥散分布是锻件获得较高强度的主要原因.锻件断口在未时效处理状态下主要为韧性断裂,而随着时效过程的进行,断裂方式逐渐转变为准解理断裂.
参考文献
| [1] | 梁维中,吉泽升,左锋,洪艳,刘洪汇,李军,刘洪德.耐热镁合金的研究现状及发展趋势[J].特种铸造及有色合金,2003(02):39-41. |
| [2] | 康鸿跃,陈善华,马永平,王忠海.镁合金在军事装备中的应用[J].金属世界,2008(01):61-64. |
| [3] | 郭学锋,魏建锋,张忠明.镁合金与超高强度镁合金[J].铸造技术,2002(03):133-136. |
| [4] | D.B. Shan;W.C. Xu;Y. Lu .Study on precision forging technology for a complex-shaped light alloy forging[J].Journal of Materials Processing Technology,2004(1/3):289-293. |
| [5] | 郝南海.上机匣等温锻造工艺研究[J].热加工工艺,1997(02):36. |
| [6] | 张洪杰,孟健,唐定骧.高性能镁-稀土结构材料的研制、开发与应用[J].中国稀土学报,2004(01):40-47. |
| [7] | Z. Yang;J.P. Li;Y.C. Guo .Precipitation process and effect on mechanical properties of Mg-9Gd-3Y-0.6Zn-0.5Zr alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(0):274-280. |
| [8] | Ke Liu;L.L. Rokhlin;F.M. Elkin;Dingxiang Tang;Jian Meng .Effect of ageing treatment on the microstructures and mechanicalproperties of the extruded Mg–7Y–4Gd–1.5Zn–0.4Zr alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2010(3):828-834. |
| [9] | S.M. He;X.Q. Zeng;L.M. Peng .Microstructure and strengthening mechanism of high strength Mg-10Gd-2Y-0.5Zr alloy[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2007(1/2):316-323. |
| [10] | Zheng, KY;Dong, J;Zeng, XQ;Ding, WJ .Precipitation and its effect on the mechanical properties of a cast Mg-Gd-Nd-Zr alloy[J].Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing,2008(1/2):44-54. |
| [11] | X.H. Shao;Z.Q. Yang;X.L. Ma .Strengthening and toughening mechanisms in Mg-Zn-Y alloy with a long period stacking ordered structure[J].Acta materialia,2010(14):4760-4771. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%