To improve the surface corrosion resistance of the alumina films fabricated by micro-arc oxidation (MAO),Al2O3 coatings at different current densities (5, 7 and 10 A/dm2) were produced on aluminum alloys by adding SiC nano-particles into electrolyte during MAO process. The morphology and phase composition of the coatings were investigated by scanning electron microscopy (SEM) and X-ray diffraction (XRD), respectively.Furthermore, the corrosion performance of the coatings was evaluated via a three-electrode system in a 3.5 wt pct NaCl solution. From the obtained morphology of alumina coatings, it was believed that the Al2O3 coatings embedded with SiC nano-particles were formed. The electrochemical impedance spectroscopy (EIS) plots and potentiodynamic polarization plots of the Al2O3 coatings with and without SiC nano-particles at different current densities reveal that the Al2O3 coatings with SiC nano-particles formed at 10 A/dm2 showed the better corrosion resistance than the other coatings produced at 5 and 7 A/dm2.
参考文献
| [1] | A. L. Yerokhin;X. Nie;A. Leyland;A. Matthews;S. J. Dowey .Plasma electrolysis for surface engineering[J].Surface & Coatings Technology,1999(2/3):73-93. |
| [2] | Y.M. Wang;B.L. Jiang;L.X. Guo;T.Q. Lei .Tribological behavior of microarc oxidation coatings formed on titanium alloys against steel in dry and solid lubrication sliding[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2006(8):2989-2998. |
| [3] | A. L. Yerokhin;X. Nie;A. Leyland;A. Matthews .Characterisation of oxide films produced by plasma electrolytic oxidation of a Ti-6Al-4V alloy[J].Surface & Coatings Technology,2000(2/3):195-206. |
| [4] | V. Raj;M. Mubarak Ali .Formation of ceramic alumina nanocomposite coatings on aluminium for enhanced corrosion resistance[J].Journal of Materials Processing Technology,2009(12/13):5341-5352. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%