通过氟钛酸改性KH858+KH580混合硅烷,配制出无铬钝化液,将其涂覆在热镀锌板上,经烘干、固化,形成无铬钝化膜.测定了钝化膜的厚度、附着力和硬度;通过中性盐雾试验,研究了钝化膜的耐化学腐蚀性能;通过Tafel极化曲线和EIS图谱,表征了钝化膜的耐电化学腐蚀性能.结果表明:钝化膜的平均厚度为5.2μm,附着力测试的被剥离面积为3%,硬度为3H,均满足国家标准,符合工业生产要求;此外,钝化膜的耐化学腐蚀和耐电化学腐蚀性能优良,相比于改性前,其性能有较大提高.
参考文献
[1] | 彭天兰,满瑞林,徐斌,乔亮杰.硅烷γ-APS协同稀土镧钝化镀锌钢板的研究[J].腐蚀科学与防护技术,2008(05):350-352. |
[2] | 何世权,钟辉,刘飞,田禾,苏燕.热浸镀锌钢板钼酸盐复合钝化膜的耐腐蚀性能[J].兰州理工大学学报,2011(01):14-16. |
[3] | 王雷,刘常升,安成强.镀锌层无机物与有机物复合无铬钝化研究进展[J].电镀与精饰,2011(03):22-26. |
[4] | 刘洪锋,何明奕,王胜民,赵晓军.热镀锌层钛盐钝化膜耐蚀性能的研究[J].热加工工艺,2011(18):138-140. |
[5] | 王典,刘建国,殷跃军,韩长智,严川伟.钛添加剂对无铬达克罗防护性能的影响[J].腐蚀科学与防护技术,2009(04):426-428. |
[6] | 郑利云,曹发和,刘文娟,陈安娜,廖晓宁,张鉴清.Q235钢在模拟自然环境下失效行为的电化学研究[J].装备环境工程,2011(04):8-15. |
[7] | Studies on adhesion characteristics and corrosion behaviour of vinyltriethoxysilane/epoxy coating protective system on aluminium[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2010(11):3508. |
[8] | 刁显珍 .二氧化钛薄膜材料的制备及其性能研究[J].功能材料,2011,42(增刊2):280-281,26. |
[9] | KONG G;LIU L Y;LU J T et al.Corrosion Behavior of Lanthanum-based Conversion Coating Modified with Citric Acid on Hot Dip Galvanized Steel in Aerated 1 M NaC1 Solution[J].Corrosion Science,2011,53:1621-1626. |
[10] | O. Lavigne;C. Alemany-Dumont;B. Normand;M.H. Berger;C. Duhamel;P. Delichere .The effect of nitrogen on the passivation mechanisms and electronic properties of chromium oxide layers[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2011(6):2087-2096. |
[11] | 曾恩,张三平,周学杰,郑俊涛,周婵.热镀锌板表面硅烷处理耐蚀性能的研究[J].装备环境工程,2010(01):22-25. |
[12] | GONZ(A)LEZ S;GIL M A;HERN(A)NDEZ J O et al.Resistance to Corrosion of Galvanized Steel Covered with an Poxypolyamide Primer Coating[J].Progress in Organic Coatings,2001,41:167-170. |
[13] | Suegama PH;de Melo HG;Recco AAC;Tschiptschin AP;Aoki IV .Corrosion behavior of carbon steel protected with single and bi-layer of silane films filled with silica nanoparticles[J].Surface & Coatings Technology,2008(13):2850-2858. |
[14] | Development of electroless Ni-Zn-P/nano-TiO_2 composite coatings and their properties[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2010(24):7377-7383. |
[15] | SHIBLI S M A;CHACKO F .Development of Nano TiO2-incorporated Phosphate Coatings on Hot Dip Zinc Surface for Good Paintability and Corrosion Resistance[J].Applied Surface Science,2011,257:3111-3117. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%