采用失重法、X射线衍射法、电化学测试、扫描电镜等手段对比分析研究了铈铝黄铜和添加微量铟的新型铝黄铜的耐蚀性能。结果表明,铈铝黄铜的平均腐蚀速率为7.3×10-3 mm/a,新型铝黄铜的腐蚀速率为6.7×10-3mm/a。添加铟后能大幅度提高极化电阻,从而减小了腐蚀电流密度,耐腐蚀性能进一步得到提高;铟的加入改善了膜的结构,含In铈铝黄铜在NaCl（3.5%）溶液中腐蚀后表面形成了一层致密、完整的腐蚀产物膜,一定程度地抑制了脱锌;铟能减少锌的析氢反应,从而进一步抑制了黄铜的脱锌腐蚀。因此微量铟的加入可以改善稀土铝黄铜的腐蚀性能。
The effect of trace indium on the corrosion resistance of rare-earth aluminum brass was studied by means of weight loss measurement,electrochemical testing,XRD and scanning electron microscopy.The results show that the average corrosion rate of the ceric aluminum brass was 7.3×10-3 mm/a,with the addition of trace indium,the polarization resistance was greatly improved and the free corrosion current density was reduced,the average corrosion rate was 6.7×10-3 mm/a.The trace In can improve the structure of the corrosion film and after corrosion in 3.5% NaCl solution,a tight and integrated corrosion film was formed on the surface of the matrix and the film can inhibit the diffusion of Zn atoms from the matrix to the solution to a certain extent.Besides,In can reduce the release of hydrogen from Zn,and thus can further inhibit the dezincification of brass.
参考文献
| [1] | Sayed SM.;Ashour EA.;Youssef GI.;El-Raghy SM. .Effect of sulfide ions on the stress corrosion behaviour of Al-brass and Cu10Ni alloys in salt water[J].Journal of Materials Science,2002(11):2267-2272. |
| [2] | 李勇,朱应禄.黄铜脱锌腐蚀的研究进展[J].腐蚀与防护,2006(05):222-225,262. |
| [3] | 邓楚平,黄伯云,苏玉长,刘东华.微量的砷、硼和稀土Ce对黄铜冷凝管耐蚀行为的影响[J].湖南电力,2007(04):9-12. |
| [4] | 程建奕,李周,唐宁,曹建国,赵学龙.含稀土HSn70-1锡黄铜的腐蚀行为研究[J].材料热处理学报,2007(05):101-104. |
| [5] | 程建奕,李周,唐宁,汪明朴,曹建国,赵学龙,杨天足.含稀土HAl77-2铝黄铜的腐蚀行为[J].中国有色金属学报,2007(08):1273-1279. |
| [6] | 张娟,李周,陈畅,唐宁,张德智.含铈铝黄铜的显微组织与性能[J].中国有色金属学报,2008(11):1989-1994. |
| [7] | 刘增才,林乐耘,刘少峰.实海暴露黄铜脱锌腐蚀行为及抑制脱锌机理研究[J].腐蚀科学与防护技术,1999(02):78-83. |
| [8] | 李伟,费锡明,汪继红,龙光斗.高氢过电位Zn-In合金电沉积规律和性能的研究[J].材料保护,2004(05):11-12. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%