采用高能球磨法制备了活性炭(AC)和TiF3共掺杂NaAlH4复合储氢材料,研究了TiF3和AC共掺杂NaAlH4后复合材料的吸/放氢性能.结果表明:共掺杂10％(质量分数)AC和3％(摩尔分数)TiF3明显降低了NaAlH4前两步放氢温度,且较单一掺杂而言,共掺杂AC和TiF3更有利于NaAlH4放氢温度的降低;160℃下NaAlH4 +TiF3+AC样品在170 min内放氢5.0％(质量分数),完成理论放氢量的93％;4次吸放氢循环后NaAlH4 +TiF3 +AC依然具有良好的循环稳定性,在160℃、真空下起始放氢以及130℃、9MPa起始吸氢条件下,NaAlH4可逆储氢量可达4.8％(质量分数).
参考文献
| [1] | DoE hydrogen .Fuel cells and infrastructure technologies program[EB/OL].http://www.eere.energy.gov/ hydrogenand fuelcells/mypp/pdfs/storage.pdf |
| [2] | Bogdanovic B;Schwickardi M .Ti-doped alkali metal aluminum hydrides as potential novel reversible hydrogen storage materials[J].Journal of Alloys and Compounds,1997,253-254:1. |
| [3] | Fan, XL;Xiao, XZ;Hou, JC;Zhang, Z;Liu, YB;Wu, Z;Chen, CP;Wang, QD;Chen, L .Reversible hydrogen storage behaviors and microstructure of TiC-doped sodium aluminum hydride[J].Journal of Materials Science,2009(17):4700-4704. |
| [4] | Xuezhang Xiao;Lixin Chen;Xinhua Wang;Shouquan Li;Changpin Chen;Qidong Wang .Reversible hydrogen storage properties and favorable co-doping mechanism of the metallic Ti and Zr co-doped sodium aluminum hydride[J].International journal of hydrogen energy,2008(1):64-73. |
| [5] | Wang P;Jensen C M .Method for preparing Ti-doped NaAlH4 using Ti powder:Observation of an unusual reversible dehydrogenation behavior[J].Journal of Alloys and Compounds,2004,379(1-2):99. |
| [6] | Leon A;Rothe J;Fichtner M .Variation and influence of the local structure around Ti in NaAlH4 doped with a Ti-based precursor[J].Journal of Physical Chemistry C,2007,111(44):16664. |
| [7] | Chengzhang Wu;Hui-Ming Cheng .Effects of carbon on hydrogen storage performances of hydrides[J].Journal of Materials Chemistry: An Interdisciplinary Journal dealing with Synthesis, Structures, Properties and Applications of Materials, Particulary Those Associated with Advanced Technology,2010(26):5390-5400. |
| [8] | Berseth, PA;Harter, AG;Zidan, R;Blomqvist, A;Araujo, CM;Scheicher, RH;Ahuja, R;Jena, P .Carbon Nanomaterials as Catalysts for Hydrogen Uptake and Release in NaAlH4[J].Nano letters,2009(4):1501-1505. |
| [9] | J. Wang;A.D. Ebner;T. Prozorov .Effect of graphite as a co-dopant on the dehydrogenation and hydrogenation kinetics of Ti-doped sodium aluminum hydride[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2005(1/2):252-262. |
| [10] | Cento C;Gislon P;Bilgili M et al.How carbon affects hydrogen desorption in NaAlH4 and Ti-doped NaA1H4[J].Journal of Alloys and Compounds,2007,437(1-2):360. |
| [11] | Bellosta von Colbe J M;Felderhoff M;Bogdanovic B et al.One-step direct synthesis of a Ti-doped sodium alanate hydrogen storage material[J].Chemical Communications,2005,37:4732. |
| [12] | Santanu Chaudhuri;Jason Graetz;Alex lgnatov .Understanding the Role of Ti in Reversible Hydrogen Storage as Sodium Alanate:A Combined Experimental and Density Functional Theoretical Approach[J].Journal of the American Chemical Society,2006(35):11404-11415. |
| [13] | Sun D L;Srinivasan S S;Chen G et al.Rehydrogenation and cycling studies of dehydrogenated NaA1H4[J].Journal of Alloys and Compounds,2004,373(1-2):265. |
| [14] | 郑时有 .轻质储氢材料的研究[D].复旦大学,2009. |
| [15] | B. Bogdanovic;U. Eberle;M. Felderhoff .Complex aluminum hydrides[J].Scripta materialia,2007(10):813-816. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%