采用Gleeble-1500型热模拟试验机对Ti-1300近β钛合金进行了等温恒应变速率压缩试验.变形温度范围为:920～1010℃,应变速率范围为:0.01～10 s-1,最大变形量为80%.根据试验数据建立了Ti-1300合金高温热变形行为的流变应力模型,得出该合金的变形激活能为177.59 kJ/mol.结合样品的显微组织分析可知,该合金在低应变速率下发生了动态再结晶,且随着温度的升高,再结晶晶粒呈现长大的趋势:在高应变速率下以动态回复为主.结果表明,为获得细小的再结晶组织,Ti-1300钛合金宜在相变点以上50～150℃的温度范围内采用较低的变形速率进行锻造.
参考文献
| [1] | 葛鹏,赵永庆,周廉.固溶条件对一种新型亚稳β钛合金时效响应的影响[J].稀有金属材料与工程,2006(05):707-710. |
| [2] | 开姆洛克胶粘剂系列在沪投产[J].材料工程,1994(10):46. |
| [3] | Sdnivasan R;Weiss I.B Titanium Alloys in the1990s[M].Warrendale:TMS,1993:283. |
| [4] | Long M;Rack H J.Titanium'95:Science and Technology[M].London:Institute of Metals,1996:316. |
| [5] | Srnivasan R .[J].Scripta Metallurgical,1992,27:925. |
| [6] | Vijayshankar M N;Ankem S.Iitanium'92:Science and Technology[M].Warrendale:TMS,1993:1733. |
| [7] | Rao K P;Hawbolt E B .[J].ASME Journal of Engineering Materials and Technology,1992,114(01):116. |
| [8] | Miaoquan Li;Hongsi Pan;Yingying Lin;Jiao Luo .High temperature deformation behavior of near alpha Ti-5.6Al-4.8Sn-2.0Zr alloy[J].Journal of Materials Processing Technology,2007(1):71-76. |
| [9] | Zener C;Hollom J H .[J].Journal of Applied Physics,1994,15(01):22. |
| [10] | Montheillet F;Dajno D;Come N.[A].Warrendle:TMS,1993:1347. |
| [11] | 朱伟勇;傅连魁.冶金工程统计学[M].Beijing:The Metallurgy Industry Press,1991 |
| [12] | Poirier J P;关德林.晶体的高温塑性变形[M].大连:大连理工大学出版社,1989:78. |
| [13] | 胡大为;渊雅琴;吴云书 .[J].金属学报,1987,23(03):242. |
| [14] | S. Gourdet;F. Montheillet .Effects of dynamic grain boundary migration during the hot compression of high stacking fault energy metals[J].Acta materialia,2002(11):2801-2812. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%