以Al-K2ZrF6-KBF4为反应体系,在高能超声下原位合成了ZrB2/A356复合材料;研究了超声功率对ZrB2颗粒尺寸、形貌、分布的影响,以及复合材料室温干滑动磨损性能。结果表明：随着超声功率的增加,复合材料中的ZrB2颗粒逐渐细化,其含量也有一定程度提高;当超声功率达到1.6kW时,出现大量ZrB2纳米颗粒,其形貌由原来的块状、柱状变为粒状,复合材料的磨损量减小到56mg,耐磨性提高到1.08,磨损面出现较明显的犁沟。
The ZrB2/A356 composite was in-situ synthetized from Al-K2ZrF6-KBF4 reaction system under high-intensity ultrasonic.The effect of ultrasonic power on ZrB2particle size,morphology and distribution was studied and the dry sliding wear property of the composite at room temperature was studied,too.The results show that the size of ZrB2 particles were fined gradually and the content of ZrB2 particles rose with the increase of ultrasonic power in certain degree.There are amounts of ZrB2 particles were found,the morphology of particles changed into granular from block and columnar,the wear loss decreased to 56 mg and the resistant wear increased to 1.08,and obvious furrows appeared on wear surface when the ultrasonic power was 1.6 kW.
参考文献
| [1] | Tongxiang Fan;Di Zhang;Guang Yang .Fabrication of in situ Al_2O_3/Al composite via remelting[J].Journal of Materials Processing Technology,2003(2):556-561. |
| [2] | Hailong Wang;Rui Zhang;Xing Hu;Chang-An Wang;Yong Huang .Characterization of a powder metallurgy SiC/Cu-Al composite[J].Journal of Materials Processing Technology,2008(1-3):43-48. |
| [3] | Tani Toshihiko .Processing,microstructure and properties of in-situ reinforced SiC matrix composites[J].Composites, Part A. Applied science and manufacturing,1999(4):419-423. |
| [4] | 余志勇,郝斌,崔华,周香林,张济山.纳米SiC颗粒增强铝基复合材料制备工艺进展[J].材料导报,2006(z2):206-208,218. |
| [5] | H. Erdem Camurlu;Filippo Maglia .Preparation of nano-size ZrB_2 powder by self-propagating high-temperature synthesis[J].Journal of the European Ceramic Society,2009(8):1501-1506. |
| [6] | 张松利,赵玉涛,陈刚,汪长勤.超声化学原位合成（Al3Zr+ZrB2）/A356复合材料的力学行为[J].中国有色金属学报,2008(12):2140-2144. |
| [7] | J. Fjellstedt;A.E.W. Jarfors .On the precipitation of TiB_2 in aluminum melts from the reaction with KBF_4 and K_2TiF_6[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(0):527-532. |
| [8] | 王俊,陈锋,孙宝德.高能超声在制备颗粒增强金属基复合材料中的作用[J].上海交通大学学报,1999(07):813-816. |
| [9] | 陈跃,邢建东,张永振,沈百令,倪锋.增强颗粒对铝基复合材料摩擦学性能的影响[J].摩擦学学报,2001(04):251-255. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%