为提高钛合金高温微动疲劳抗力,利用离子辅助电弧沉积技术在TC17钛合金表面制各了TiN/Ti复合膜层,研究了膜层的剖面成分分布、膜基结合强度、膜层显微硬度、韧性、常规摩擦学性能以及抗高温微动疲劳性能.结果表明:利用离子辅助电弧沉积技术可以获得硬度高、韧性好、膜基结合强度和承载能力优异的TiN/Ti复合膜层,该膜层具有良好的抗磨和减摩性能,能够显著地提高TC17钛合金在350℃高温环境下的常规磨损和微动疲劳抗力.然而,TC17钛合金表面喷丸强化后进行离子辅助沉积TiN/Ti复合膜,由于喷丸层残余压应力的显著松弛以及膜层易于开裂和脱落的缘故,微动疲劳抗力则不及喷丸强化或TiN/Ti复合膜单独作用.
参考文献
| [1] | James C W et al.[J].Acta Materials,2003,51:5775. |
| [2] | Hoeppner D W .[J].Tribology International,2006,39:1271. |
| [3] | Ray A K et al.[J].ENGINEERING FAILURE ANALYSIS,2004,11:613. |
| [4] | Hutson A L et al.[J].International Journal of Fatigue,2002,24(12):1223. |
| [5] | Wei R et al.[J].Surface and Coatings Technology,2004,192(02):177. |
| [6] | Liu Daoxin et al.[J].Surface and Coatings Technology,1999,116-119:234. |
| [7] | Hyukjae L et al.[J].Materials Science and Engineering,2005,A390:227. |
| [8] | Sung JH.;Kim SS.;Kim TH. .Fretting damage of TiN coated zircaloy-4 tube[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2001(1):658-664. |
| [9] | 刘道新,陈华,何家文.等离子渗氮与喷丸强化复合改进钛合金抗微动损伤性能[J].材料热处理学报,2001(03):49-54. |
| [10] | 刘道新,唐宾,陈华,何家文.钛合金表面离子束增强沉积MoS2基膜层及其性能[J].中国有色金属学报,2001(03):454-460. |
| [11] | Lee HY;Kim YM;Jung WS;Han JG;Kim JH;Bae EH .Synthesis of WC-Ni films using an arc ion plating system with attached solenoid soil[J].Surface & Coatings Technology,2005(1/3):303-308. |
| [12] | 张晓化,刘道新,高广睿.喷丸强化因素对Ti811合金高温微动疲劳抗力的影响[J].稀有金属材料与工程,2005(12):1985-1989. |
| [13] | Fridrici V.;Kapsa P.;Fouvry S. .Effect of shot peening on the fretting wear of Ti-6Al-4V[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2001(1):642-649. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%