为了改善多壁碳纳米管(MWNTS)在溶剂N,N-二甲基乙酰胺(DMAc)中的分散性,提高MWNTs与芳纶1313(PMIA)基体界面的结合性能,用混酸对MWNTs进行了处理,用FT-IR对处理前后的MWNTs进行了表征,发现处理后的MWNTs表面接上了羧基.通过溶液共混的方法制得了PMIA/MWNTs纳米复合薄膜,并用SEM和TEM对其进行了表征,发现处理后的MWNTs在PMIA基体中的分散更为均匀.
参考文献
| [1] | Gao JB;Zhao B;Itkis ME;Bekyarova E;Hu H;Kranak V;Yu AP;Haddon RC .Chemical engineering of the single-walled carbon nanotube-nylon 6 interface[J].Journal of the American Chemical Society,2006(23):7492-7496. |
| [2] | Zhu Jiang;Kim L D;Peng Haiqing et al.[J].Nano Letters,2003,3(08):1107-1113. |
| [3] | Kumar S.;Dang TD.;Arnold FE.;Bhattacharyya AR.;Min BG.;Zhang XF. Vaia RA.;Park C.;Adams WW.;Hauge RH.;Smalley RE.;Ramesh S.;Willis PA. .Synthesis, structure, and properties of PBO/SWNT composites[J].Macromolecules,2002(24):9039-9043. |
| [4] | Zhang Xiefei;Liu Tao;Sreekumar T V et al.[J].Nano Letters,2003,3(09):1285-1288. |
| [5] | 黄大庆,丁鹤雁,刘俊能.碳纳米管/导电聚苯胺纳米复合纤维的合成与表征[J].功能材料,2003(02):164-166,169. |
| [6] | Chen Jian;Hamon M A;Haddon R C et al.[J].Science,1998,282:95-98. |
| [7] | 方芳,张清华,常振军,陈大俊.碳纳米管/聚苯乙烯复合材料的制备及导电性能研究[J].功能材料,2007(04):659-661. |
| [8] | Sabba Y;Thomas E L .[J].Macromolecules,2004,37:4815-4820. |
| [9] | Hong C E;Lee J H;Advani S E .[J].Composites Science and Technology,2007,67:1027-1034. |
| [10] | 李艳亮,程斌,沈曾民.酸处理对多壁纳米碳管形态的影响[J].北京化工大学学报(自然科学版),2004(04):60-64. |
| [11] | 新田英昭;佐藤和彦;松村俊一 等.[P].CN:1720295A,2006-1-11. |
| [12] | HU Xiaodong;Kenneth S .[P].WO:03/085049A1,2003-10-16. |
| [13] | 邢哲,夏延致,王川.耐紫外线芳纶1313的制备及力学性能研究[J].陕西科技大学学报（自然科学版）,2007(05):67-70. |
| [14] | Britto PJ.;Rubio A.;Alonso JA.;Ajayan PM.;Santhanam KSV. .Improved charge transfer at carbon nanotube electrodes[J].Advanced Materials,1999(2):154-157. |
| [15] | Liu J;Rinzler A G;Smalley R E .[J].Science,1998,280:1253-1256. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%