PNW-PMS-PZT压电陶瓷准同型相界的压电性能研究

无机材料学报, 2005, 20(4): 988-992.

PNW-PMS-PZT压电陶瓷准同型相界的压电性能研究

裴志斌 , 杜红亮 , 车俊 , 魏晓勇 , 屈绍波

1.1. 空军工程大学理学院, 西安 710051

2. 2. 西安交通大学电子陶瓷与器件教育部重点实验室, 西安 710049

1.1. The College of Science

Air Force Engineering University

Xi an 710051

China

2. 2. Electronic Materials Research Laboratory

Key Laboratory of Ministry of Education

Xi an Jiaotong University

关键词： PNW-PMS-PZT压电陶瓷 , morphotropic phase boundary , rhombohe-dral , tetragonal

Piezoelectric Properties of Morphotropic Phase Boundary for PNW-PMS-PZT Piezoelectric Ceramics

PEI Zhi-Bin , DU Hong-Liang , JU Jun , WEI Xiao-Yong , QU Shao-Bo

Keywords： PNW-PMS-PZT piezoelectric ceramics , 准同型相界 , 三方相 , 四方相

采用传统陶瓷工艺制备了PNW—PMS—PZT四元系压电陶瓷,分析了陶瓷样品的相结构组成,结果表明,所有陶瓷样品的相结构为纯钙钛矿相结构;研究了室温下PMS含量,PNW 含量和Zr/Ti的变化对准同型相界的影响规律,实验表明随着PMS、PNW含量和Zr/Ti的增加,材料体系逐渐由四方相向三方相过渡,获得了处于准同型相界附近的材料组成:PMS 的含量在5—6mol%、PNW的含量在2—3mol%、PZT的含量在91—93mol%、Zr/Ti的变化靠近50/50,同时具有高的机电性能.

The piezoelectric ceramics (PNW-PMS-PZT) were prepared by traditional ceramics process. The phase
structure of all ceramics samples was analyzed. Results show that the pure perovskite phase is in all ceramics specimens researched. The effect of the content
of PMS, PNW and Zr/Ti ratio on the region of morphotropic phase boundary for PNW-PMS-PZT piezoelectric ceramics was studied. Results show
that the phase structure of PNW-PMS-PZT piezoelectric ceramics changes from tetragonal to rhombohedral with the increase of the amount of PMS, PNW and the ratio of Zr/Ti
in the system. The composition of PNW-PMS-PZT piezoelectric ceramics near the morphotropic phase boundary obtained is the content of PMS: 5～6mol%; the content of PNW: 2～3mol%; the content of PZT: 91～93mol%; the ratio of Zr/Ti: 50/50. At the
same time, there is high piezoelectricity near the morphotropic phase boundary.

参考文献

[1]

Richard E. EITEL, Cliven A. RANDALL, Thomas R. SHROUT, et al. Jpn. J. Appl. Phys., 2002, 41 (4): 2099--2104.
[2] Hideki ISHII, Hajime NAGATA, Tadashi TAKENAKA. Jpn. J. Appl. Phys., 2001, 40 (9): 5660--5663.
[3] Masao KONDO, Mineharu TSUKADA, Kazuaki KURIHARA. Jpn. J. Appl. Phys., 1999, 38 (9): 5539--5543.
[4] 李振荣, 张良莹, 姚熹(LI Zhen-Rong, et al). ?硅酸盐学报(Journal of the Chinese Ceramic Society), 2000, 28 (3): 199--203.
[5] 刘涛, 孙清池, 左孝杰. 硅酸盐通报, 2003, 2: 30--33.
[6] GAO Yongkang, CHEN Yun-Han, Dwight Viehland, et al. Jpn. J. Appl. Phys., 2001, 40 (2): 687--693.
[7] 周桃生. 材料导报, 1994, 4: 39--42.
[8] Yoo J H, Lee Y W, Yoon K H, et al. Jpn. J. Appl. Phy., 2001, 40 (5): 3256--3259.
[9] FENG XIA, XI YAO. J. Mater. Sci. Lett., 2001, 36: 247--253.
[10] ZHU W Z, YAN M. J. Mater. Sci. Lett., 2001, 20: 1527--1529.
[11] 贺连星, 李承恩(HE Lian-Xing, et al). 无机材料学报(Journal of Inorganic Materials), 2000, 15 (2): 293--298.
[12] 李标荣, 莫以豪, 王莜珍. 无机介电材料, 第1版. 上海: 上海科学技术出版社, 1986. 6--7.