为了解决目前无溶剂环氧聚氨酯涂料生产中由原材料异氰酸酯有毒,以及对湿度敏感等问题给生产与运输带来的不便,本研究以环氧树脂与二氧化碳反应制得的环氧-环碳酸酯为甲组分,以端氨基聚醚和端巯基乙酸一缩二乙二醇酯为乙组分,配以适当的颜填料和助剂,制备了一种新型双组分重防腐涂料.对所制得的防腐涂料性能、影响因素以及配方设计进行讨论,得出了最佳配方.性能测试结果表明涂层防腐性能及物理机械性能均达到重防腐涂料的行业标准.
参考文献
| [1] | Hidetoshi Tomita;Fumio Sanda;Takeshi Endo .Reactivity Comparison of Five- and Six-Membered Cyclic Carbonates with Amines: Basic Evaluation for Synthesis of Poly(hydroxyurethane)[J].Journal of Polymer Science, Part A. Polymer Chemistry,2001(1):162-168. |
| [2] | Ochiai B;Inoue S;Endo T .One-pot non-isocyanate synthesis of polyurethanes from bisepoxide, carbon dioxide, and diamine[J].Journal of Polymer Science, Part A. Polymer Chemistry,2005(24):6613-6619. |
| [3] | 李振荣 .碳酸酯化大豆油的合成及其胺解制备非异氰酸酯聚氨酯[D].中国科学院山西煤炭化学研究所,2009. |
| [4] | ROKICK G .Aliphatic cyclic carbonates and spiroorthocarbonates as monomers[J].Progress in Polymer Science,2000,25:259-342. |
| [5] | 黄丽.聚合物复合材料[M].北京:中国轻工业出版社,2008 |
| [6] | GARIPOV R M;SYSOEV V A;MIKHEEV V V et al.Reactivity of cyclocarbonate groups in modified epoxy-am ine composition[J].Doklady Physical Chemistry,2003,393:289-292. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%