利用热处理和化学相分析对薄板坯连铸连轧低碳铝镇静钢中AlN的沉淀析出行为进行了试验研究.结果显示,在薄板坯连铸连轧的低碳铝镇静钢中仅有很少量的氮被固定为AlN,大部分氮仍为自由氮,其原因是在薄板坯连铸连轧流程中的连铸出坯、均热、连轧和层流冷却等阶段,AlN在钢中很少沉淀析出.在热轧钢板卷取后的缓慢空冷过程中可以沉淀析出少量的AlN,这些AlN不能起到细化晶粒的作用.
参考文献
[1] | Mohamed Sennour;Claude Esnouf .Contribution of advanced microscopy techniques to nano-precipitates characterization: case of AlN precipitation in low-carbon steel[J].Acta materialia,2003(4):943-957. |
[2] | Michel J P;Jonas J J .Precipitation Kinetics and Solute Strengthening in High Temperature Austenite Containing Al and N[J].Acta Metallurgica,1981,29(03):513. |
[3] | Erasmus L A .Effect of Aluminum Additions on Forgeability,Austenite Grain Coarsening Temperature,and Impact Proper-ties of Steel[J].Journal of the Iron and Steel Institute,1964,202(01):32. |
[4] | Croft N H;Entwisle A R;Davies G J .Origins of DendriticAIN Precipitates in Aluminum Killed Steel Castings[J].Metals and Technology,1983,lO(04):125. |
[5] | Gladman T;Pickering F B .Grain-Coarsening of Austenite[J].Journal of the Iron and Steel Institute,1967,205(06):653. |
[6] | 刘阳春 .薄板坯连铸连轧低碳铝镇静钢N、Al的作用与控制研究[D].北京:北京科技大学,2007. |
[7] | 陈襄武.炼钢过程的脱氧[M].北京:冶金工业出版社,1991 |
[8] | 刘清友,梁小恺,王雪莲,李德刚,董瀚.薄板坯连铸连轧流程低碳Al镇静钢组织细化原因探讨[J].钢铁,2005(08):65-69. |
[9] | Wilson F G;Gladman T .Aluminum Nitride in Steel[J].International Materials Reviews,1988,33(05):221. |
[10] | 刘正东,程杰锋,董瀚,干勇.热轧带钢卷带及其冷却过程AlN沉淀析出模拟研究[J].钢铁,2004(03):38-42. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%