测量锌阳极在海泥和含硫酸盐还原菌(SRB)海泥中构成的宏电池中的腐蚀,研究了SRB对海泥中纯锌阳极材料的腐蚀行为的影响.结果表明,SRB能快速破坏纯锌的表面钝化膜,提高锌阳极在海泥中的自腐蚀速率.在含SRB和无SRB海泥构成的宏电池体系中,含菌海泥中的锌试样为电偶对的阳极,腐蚀增大;无菌海泥中的试样为电偶对的阴极,腐蚀受到抑制.
参考文献
| [1] | F.S.Li,M.Z.An,G.Z.Liu,D.X.Duan,Effects of sulfidation of passive film in the presence of SRB on the pitting corrosion behaviors of stainless ateels,Materials Chemistry and Physics,113,971(2009) |
| [2] | P.J.Antony,R.K.Singh Raman,R.Mohanram,Pradeep Kumar,R.Raman,Influence of thermal aging on sulfatereducing bacteria (SRB)-influenced corrosion behaviour of 2205 duplex stainless steel,Corrosion Science,50,1858(2008) |
| [3] | E.Ilhan-Sungur,N.Cansever,A.Cotuk,Microbial corrosion of galvanized steel by a freshwater strain of sulphate reducing bacteria (Desulfovibrio sp),Corrosion Science,49,1097(2007) |
| [4] | P.J.Antony,Shobhana Chongdar,Pradeep Kumar,R.Raman.Corrosion of 2205 duplex stainless steel in chloride medium containing sulfate-reducing bacteria,Electrochimica Acta,52,3985(2007) |
| [5] | H.Castaneda,X.D.Benetton,SRB-biofilm influence in active corrosion sites formed at the steel-electrolyte interface when exposed to artificial seawater conditions,Corrosion Science,50,1169(2008) |
| [6] | T.S.Rao,A.J.Kora,B.Anupkumar,S.V.Narasimhan,R.Feser,Pitting corrosion of titanium by a freshwater strain of sulphate reducing bacteria (Desulfovibrio vulgaris),Corrosion Science,47,1071(2005) |
| [7] | X.T.Chang,S.G.Chen,G.H.Gao,Y.S.Yin,S.Cheng,T.Liu,Electrochemical behavior of microbiologically influenced corrosion on Fe3Al in marine environment,Acta Metall,22,313(2009) |
| [8] | DU Yili,LI Jin,CUI Lianjun,ZHAO Zhejun,Effect of biofilm on microbiologically influence corrosion of Cu30Ni alloy,Corrosion Science and Protection Technology,19(6),401(2007)(杜一立,李进,崔连军,赵哲军,生物膜在B30合金微生物腐蚀中的作用,腐蚀科学与防护技术,19(s),401(2007)) |
| [9] | WU Jiang,LIU Guifu,ZHANG Jie,Development of High Temperature Zinc Alloy Sacrificial Anode,Non-Ferrous Mining And Metallurgy,23(3),34(2007)(武江,刘贵甫,张洁,耐高温锌基合金牺牲阳极的研制,有色矿冶,23(3),34(2007)) |
| [10] | FU Yan,ZHAI Xiujing,WANG Jie,LI Tao,LIU Zhongbao,ZHANG Xiaoshun,Sacrifices Anode Materials of Zinc Alloy Systems Adding Rare Earth Elements,Chinese Rare Earths,26(1),49(2005)(符岩,翟秀静,王杰,李涛,柳忠宝,张晓顺,添加稀土元素的锌基合金牺牲阳极的研究,稀土,20(1),49(2005)) |
| [11] | LONG Jinming,GUO Zhongcheng,FAN Aimin,HAN Xiayun,Sacrificial Anode Materials and their Application in Corrosion Prevention of Metals,Yunnan Metallurgy,31(3),142-148(2002)(龙晋明,郭忠诚,樊爱民,韩夏云,牺牲阳极材料及其在金属防腐工程中的应用,云南冶金,31(3),142(2002)) |
| [12] | Y.L.Huang,Corrosion failure of marine steel in sea-mud containing sulfate reducing bacteria.Materials and Corrosion,55,124(2004) |
| [13] | G.Cabrera,R.Perez,J.M.Gomez,A.Abalos,D.Cantero,Toxic effects of dissolved heavy metals on Desulfovibrio vulgaris and Desulfovibrio sp Strains,Journal of Hazardous Materials,135,40(2006) |
| [14] | V.P.Utgikar,H.H.Tabak,J.R.Haines,R.Govind,Quantification of toxic and inhibitory impact of copper and zinc on mixed cultures of sulfate-reducing bacteria,Biotechnology and Bioengineering,82,306(2003) |
| [15] | S.R.Poulson,P.J.S.Colberg,J.I.Drever,Toxicity of heavy metals (Ni,Zn) to Desulfovibrio desulfuricans,Geomicrobiol Journal,14,41(1997) |
| [16] | S.Azabou,T.Mechichi,S.Sayadi,Zinc precipitation by heavy-metal tolerant sulfate-reducing bacteria enriched on phosphogypsum as a sulfate source,Minerals Engineering,20,173(2007) |
| [17] | LIU Jing,XU Liming,ZHENG Jinshen,A study on corrnsion behavior under the biofilm of sulfate-reducing bacteria on Cu-Zn alloy,Corrosion Science and Protection Technology,21(6),345(2001)(刘靖,许立铭,郑家,硫酸盐还原菌生物膜下Cu-Zn合金的腐蚀研究,中国腐蚀与防护学报,21(6),345(2001)) |
| [18] | SUN Cheng,HAN Enhou,Effects of sulfate reducing bacteria on corrosion of zinc in marine sediment,The Chinese Journal of Nonferrous Metals,13(5),1262(2003)(孙成,韩恩厚,硫酸盐还原菌对海底土中锌腐蚀的影响,中国有色金属学报,13(5),1262(2003)) |
| [19] | C.M.Xu,Y.H.Zhang,G.X.Cheng,W.S.Zhu,Pitting corrosion behavior of 316 L stainless steel in the media of sulphate-reducing and iron-oxidizing bacteria,Materials Characterization,59,245(2008) |
| [20] | J.Z.Duan,B.R.Hou,Z.G.Yu,Characteristics of sulfide corrosion products on 316L stainless steel surfaces in the presence of sulfate-reducing bacteria,Materials Science and Engineering C,26,624(2006) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%