采用氧化还原引发体系,反相悬浮法低温合成AA/AM共聚型吸水树脂.研究了不同引发体系、单体组成、交联剂和引发剂浓度、温度、单体中和度对共聚物吸液能力的影响.与单一引发剂相比,采用复合引发体系,反应温度降低,聚合时间缩短,产物吸水速度和吸液能力高于聚丙烯酸钠,保水性略低于后者.共聚物最大吸液能力为:Q去离子水=970 mL/g,Q生理盐水=129 mL/g,Q人工尿=130 mL/g.
参考文献
| [1] | Lee WF.;Hsu CH. .Superabsorbent polymeric material. V. Synthesis and swelling behavior of sodium acrylate and sodium 2-acrylamido-2-methylpropanesulfonate copolymeric gels[J].Journal of Applied Polymer Science,1998(2):229-237. |
| [2] | Lee WF.;Yeh PL. .SUPERABSORBENT POLYMERIC MATERIALS .3. EFFECT OF INITIAL TOTAL MONOMER CONCENTRATION ON THE SWELLING BEHAVIOR OF CROSSLINKED POLY(SODIUM ACRYLATE) IN AQUEOUS SALT SOLUTION[J].Journal of Applied Polymer Science,1997(12):2371-2380. |
| [3] | Kiatkamjornwong S;Phunchareon P .[J].Journal of Applied Polymer Science,1999,72(10):1349-1366. |
| [4] | Kiatkamjornwong S;Siwarungson N;Ngabunsri A .[J].Journal of Applied Polymer Science,1999,73(11):2273-2291. |
| [5] | 路建美;朱秀林;纪顺俊 等.[J].石油化工,1998,27(05):332-335. |
| [6] | 解秀清;孙祖德 .[J].现代塑料加工应用,2001,12(06):60-62. |
| [7] | 郑邦乾,张洁辉.高吸水性树脂粒径与性能的研究[J].高分子材料科学与工程,1994(04):119-124. |
| [8] | Makamura K;Hatakeyama T;Hatakeyama H .[J].Polymer Journal,1984,20(01):61. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%