通过共混方式制备了超支化水性聚氨酯(SWHBPU)共混改性聚氨酯.采用黏度测试表征了的共混乳液的流变性能,通过静态拉伸测试和差示扫描量热法(DSC)考察了共混胶膜的力学性能和热性能,并利用透射电镜(TEM)研究了胶膜微观结构.研究结果表明,SWHBPU的添加可以有效降低聚氨酯乳液的黏度;共混聚氨酯胶膜拉伸强度和断裂伸长率均得到提高,最大升幅分别为124.69％和20.13％,而△Tg和软硬段微相分离在SWHBPU质量分数为6％时达到最大值,表明力学性能的提高是由聚氨酯微相分离程度的增大造成的.
参考文献
| [1] | Bao, F.;Shi, W. .Synthesis and properties of hyperbranched polyurethane acrylate used for UV curing coatings[J].Progress in Organic Coatings: An International Review Journal,2010(4):334-339. |
| [2] | 田星,李杰,罗运军.超支化水性聚氨酯共混改性聚氨酯乳液的性能研究[J].北京理工大学学报,2012(11):1195-1199. |
| [3] | 田星,李杰,罗运军.硬脂酸封端超支化水性聚氨酯的合成及表征[J].高分子材料科学与工程,2013(04):25-28,32. |
| [4] | Chen SJ;Cao Q;Jing B;Cai YL;Liu PS;Hu JL .Effect of microphase-separation promoters on the shape-memory behavior of polyurethane[J].Journal of Applied Polymer Science,2006(6):5224-5231. |
| [5] | Kojio K;Nakashima S;Furukawa M .Microphase-separated structure and mechanical properties of norbornane diisocyanate-based polyurethanes[J].Polymer: The International Journal for the Science and Technology of Polymers,2007(4):997-1004. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%