以玻璃包覆Co58Fe4.5Si13.5B14非晶微丝为研究对象,对经氢氟酸溶液腐蚀不同时间的微丝和不同直径的原丝进行了力学性能评价和断口形貌分析.结果表明,玻璃包覆非晶微丝的断裂过程是弹性变形.外径为28μm、内径为8.8μm的微丝经氢氟酸溶液腐蚀,刚去掉玻璃包覆层时裸丝的抗拉强度最大,可达到3545MPa,应变量为1.96%;若微丝经酸液腐蚀仍存在玻璃层,当腐蚀时间为40s时,抗拉强度和延伸率达到该阶段的最大值,分别为724MPa和1.3%;同时玻璃包覆Co68Fe4.5Si13.5B14非晶微丝具有尺寸效应,微丝的抗拉强度随直径的减小而增大.
参考文献
| [1] | Manh-Huong Phan;Hua-Xin Peng .Giant magnetoimpedance materials: Fundamentals and applications[J].Progress in materials science,2008(2):323-420. |
| [2] | Zhukova V;Zhukov A;Larin V et al.Magnetic and mechanical properties of magnetic glass-coated microwires with different glass coating[J].Materials Science Forum,2005,480-481:293. |
| [3] | Vazquez, M;Adenot-Engelvin, AL .Glass-coated amorphous ferromagnetic microwires at microwave frequencies[J].Journal of Magnetism and Magnetic Materials,2009(14):2066-2073. |
| [4] | C. Garcia;V. Zhukova;M. Ipatov .High-frequency GMI effect in glass-coated amorphous wires[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2009(1):9-12. |
| [5] | 何璞祯,王自东,王护利,张鸿,李向明,王宪军,侯志坚.玻璃包覆铁基微丝的微波电磁特性[J].纳米技术与精密工程,2009(02):114-118. |
| [6] | Zhukova V;Blanco JM;Ipatov M;Zhukov A;Garcia C;Gonzalez J;Varga R;Torcunov A .Development of thin microwires with low Curie temperature for temperature sensors applications[J].Sensors and Actuators, B. Chemical,2007(1):318-323. |
| [7] | Valenzuela R;Fessant A;Gieraltowski J;Tannous C .Effect of the metal-to-wire ratio on the high-frequency magnetoimpedance of glass-coated CoFeBSi amorphous microwires[J].Sensors and Actuators, A. Physical,2008(2):533-537. |
| [8] | Gotō T;Kazuhiro N .Mechanical properties of high strength and high toughness metallic filament composites with epoxy and poly matrices[J].Journal of Materials Science,1987,22(07):2357. |
| [9] | Donald I W;Metcalfe B L;Bye A D .Preparation of a novel unidirectionally aligned microwire-reinforced glass matrix composite[J].Journal of Materials Science Letters,1988,7(09):964. |
| [10] | Zhukova V.;Larin VS.;Zhukov A. .Stress induced magnetic anisotropy and giant magnetoimpedance in Fe-rich glass-coated magnetic microwires[J].Journal of Applied Physics,2003(2):1115-1118. |
| [11] | Zhukov A. .Glass-coated magnetic microwires for technical applications[J].Journal of Magnetism and Magnetic Materials,2002(1):216-223. |
| [12] | Goto T .Fe-B and Fe-Si-B system alloy filaments produced by glass-coated melt spinning[J].Trans Japan Institute of Metals,1980,21:219. |
| [13] | Gotō T;Yoshino A .Preparation of ductile high strength Cr and Co base filaments by glass-coated melt spining[J].Trans Japan Institute of Metals,1985,26(08):57. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%