采用金相显微镜、扫描电镜、能谱分析、透射电镜和性能测试等方法,研究了固溶温度对22Cr双相不锈钢显微组织和性能的影响.结果表明:在950～1150 ℃范围,实验钢中α、γ两相含量与固溶温度呈近似直线关系;材料的显微硬度(HV)和强度(σb)先降后升,在1050 ℃时达到最小值;当固溶温度为950 ℃,组织中出现了σ相,σ相是导致22Cr双相不锈钢塑性、韧性下降的主要原因;随着固溶温度的升高,Cr、Mo的分配系数K变小,Ni的分配系数K增大,表明合金元素在α和γ相中浓度差别变小.
参考文献
| [1] | I. Calliari;M. Zanesco;E. Ramous .Effects of Isothermal Ageing and Continuous Cooling after Solubilization in a Duplex Stainless Steel[J].Journal of Materials Engineering and Performance,2007(1):109-112. |
| [2] | 吴玖.双相不锈钢[M].北京:冶金工业出版社,1999 |
| [3] | 向导.科技成就克拉2气田[J].中国石油石化,2005(01):60-61. |
| [4] | Nilsson J O et al.Influence of isothermal phase transformations on toughness and pitting corrosion of super duplex stainless steel SAF 2507[J].Materials Science and Technology,1993,9(07):545. |
| [5] | Michael Pohl;Oliver Storz;Thomas Glogowski .Effect of intermetallic precipitations on the properties of duplex stainless steel[J].Materials Characterization,2007(1):65-71. |
| [6] | Hosni M.Ezuber;A.El-Houd;F.El-Shawesh .Effects of sigma phase precipitation on seawater pitting of duplex stainless steel[J].Desalination: The International Journal on the Science and Technology of Desalting and Water Purification,2007(1/3):268-275. |
| [7] | 余增华 .金属耐蚀材料[J].腐蚀与防护,2001,22(07):321-324. |
| [8] | 胡赓祥;钱苗根.金属学[M].上海:上海科学技术出版社,1980 |
| [9] | 宋志刚,陈斌,郑文杰,王汉东,宗玉生.固溶温度对00Cr22Ni5Mo3N钢组织及力学性能的影响[J].钢铁研究学报,2004(06):47-50. |
| [10] | 李奇志,李慧中.热处理对双相不锈钢组织与性能的影响[J].湖南有色金属,2006(01):31-33. |
| [11] | 何天荣.双相不锈钢及其特殊性能与应用[J].南方金属,2005(01):1-3. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%