研究了喷射成形和铜模吸铸法制备的La62Al15.7(Cu,Ni)22.3块体非晶合金的晶化行为.结果表明,两种工艺制备的非晶合金晶化过程都为三级晶化,晶化的顺序为:非晶→非晶+ La→非晶+La+Al3La→非晶+La+ Al3La+富Cu和Ni的未知相.结合晶化动力学计算和退火晶化实验结果表明,低温(<503 K)时,喷射成形La62Al15.7(Cu,Ni)22.3非晶合金的热稳定性优于铜模吸铸La62Al15.7(Cu,Ni)22.3非晶合金,高温(>553 K)时结果相反.
参考文献
[1] | Wang W H et al.[J].Materials Science and Engineering,2004,44:45. |
[2] | Jorg F. Loffler .Bulk metallic glasses[J].Intermetallics,2003(6):529-540. |
[3] | Song G S et al.[J].Materials Science and Engineering,1994,A179-180:249. |
[4] | Tsao C Y A et al.[J].Materials Science and Engineering,2005,A404:49. |
[5] | 董亭义,杨滨,何建平,张勇.气雾化和喷射成形制备大尺寸La62Al15.7(Cu,Ni)22.3非晶合金[J].金属学报,2008(06):659-664. |
[6] | Tan H et al.[J].Acta Materialia,2003,51:4551. |
[7] | Zhang Y et al.[J].Materials Science and Engineering,2004,A375-377:436. |
[8] | Fan C et al.[J].ApplPhys Left,1999,75:340. |
[9] | Chan K C et al.[J].Intermetallics,2007,15:500. |
[10] | Wang Qing et al.[J].Journal of Non-Crystalline Solids,2007,353:3421. |
[11] | 武慧敏,孙威,张泽,刘丽,张涛.Zr65Cu12.5Ni10Al7.5Ag5玻璃合金初期晶化结构的电子显微分析[J].稀有金属材料与工程,2008(05):823-826. |
[12] | Jiang Q K et al.[J].Journal of Alloys and Compounds,2006,424:183. |
[13] | Jiang Q K et al.[J].Acta Materialia,2007,55:4409. |
[14] | 梅金娜,李金山,寇宏超,邢力谦,傅恒志,周廉.Ti40Zr25Ni8Cu9Be18非晶合金的晶化行为研究[J].稀有金属材料与工程,2007(07):1215-1218. |
[15] | Ozawa T .[J].Journal of Thermal Analysis,1970,2:301. |
[16] | 李余增.热分析[M].北京:清华大学出版社,1987:84. |
[17] | Hyun-Joon Jun et al.[J].Materials Science and Engineering,2007,A448-451:526. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%