以Li4SiO4为母体,叶蜡石为原料的Li8Al1-xSi2xP1-xO8系统的锂快离子导体,经高温固相反应制得.X射线衍射分析结果表明该系统在0.5＜x＜0.9的组成范围内形成单一的固溶体相,其空间群为P21/m,导电性能测试结果表明x=0.6的合成物具有最高的电导率,在673K时其电导率达到2.6×10-2S/cm,其活化能为60.73kJ/mol(温度区间373～673K).
参考文献
| [1] | Wang Wenji;Guo Zhenshan.Solid State Ionics:Science &Technology[M].Singapore:World Scientific Publishing Co,1998:335-338. |
| [2] | Wang Wenji;Liu Xingfeng .[J].Solid State Ionics,1996,89:165-168. |
| [3] | Wang Wenji;Zhang Yurong .[J].Solid State Ionics,1996,88:281-284. |
| [4] | 林祖.快离子导体[M].上海:上海科学技术出版社,1983 |
| [5] | 戴安邦;沈孟长.元素周期表[M].上海:上海科学技术出版社,1988 |
| [6] | Jackowska K;West A R .[J].Journal of Materials Science,1983,18:2380-2384. |
| [7] | Quintana P;Velasco F;West A R .[J].Solid State Ionics,1989,34:149-155. |
| [8] | Garcia A;Torres-trevino G;West A R .[J].Solid State Ionics,1990,40-41:13-17. |
| [9] | Takahito Suzuki;Kenji Yoshida .[J].Solid State Ionics,1997,104:27-33. |
| [10] | Yuria Saito;Takashi Asai;Kazuaki Ado et al.[J].Solid State Ionics,1990,40/41:34-37. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%