传统的TFA-MOD法制备YBa2Cu3O7-x薄膜,采用Y、Ba、Cu 3种金属的三氟醋酸盐(TFA)为先驱体,在热分解时,会产生大量的HF气体,即使通过将近20h的缓慢升温过程来对薄膜进行热分解,也难以获得较为光洁的表面,从而无法实现厚膜的制备.本文提出了一种新的含氟溶胶-凝胶工艺,通过减少溶胶中F的含量,并利用二乙醇胺做修饰剂,缩短了热分解时间,提高了薄膜的表面光洁度.利用该方法在(010)LaAlO3衬底上制备了具有良好c轴取向,临界转变温度为89K的YBCO超导薄膜.
参考文献
| [1] | Kumagai T;Manabe T et al.[J].Japanese Journal of Applied Physics,1990,29(06):L940-L942. |
| [2] | Yang Y X;Howson M A;Milne S J .[J].Journal of Non-crystalline Solids,1992,147-148:715-719. |
| [3] | Mclntyre P C;Cima N J;Ng M F .[J].Journal of Applied Physics,1990,68:4183. |
| [4] | McIntyre P C;Cima M J et al.[J].Journal of Applied Physics,1992,71(04):15. |
| [5] | McIntyre P C;Cima M J .[J].Journal of Applied Physics,1995,77(10):15. |
| [6] | Araki T;Yamagiwa K;Hirabayashi I .[J].CRYOGENICS,2001,41:675-681. |
| [7] | Dawley JT.;Clem PG.;Boyle TJ.;Ottley LM.;Overmyer DL.;Siegal MP. .Rapid processing method for solution deposited YBa2Cu3O7-delta thin films[J].Physica, C. Superconductivity and its applications,2004(1/2):143-151. |
| [8] | Tokunaga Y;Honjo T et al.[J].Cryogenics,2004,44:817-822. |
| [9] | Castano O.;Cavallaro A.;Palau A.;Gonzalez J.C.;Rosell M.;Puig T.;Pinol S.;Mestres N.;Sandiumenge F.;Pomar A.;Obradors X. .Influence of porosity on the critical currents of trifluoroacetate-MOD YBa<SUB>2</SUB>Cu<SUB>3</SUB>O<SUB>7</SUB> films[J].IEEE Transactions on Applied Superconductivity: A Publication of the IEEE Superconductivity Committee,2003(2):2504-2507. |
| [10] | Smith J.A.;Cima M.J.;Sonnenberg N. .High critical current density thick MOD-derived YBCO films[J].IEEE Transactions on Applied Superconductivity: A Publication of the IEEE Superconductivity Committee,1999(2):1531-1534. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%