By applying nanotechnology, a new type of silver/graphite (AgC) electrical contact was fabricated and characterized. The AgC coating powders were obtained through high-energy ball milling and reducer liquid spraying-coating method. The as-prepared powders were examined by transmission electron microscope (TEM), scanning electron microscope (SEM), and X-ray diffraction (XRD). The results show that the thickness of graphite flakes milled for 10 h is about 50-60 nm and the AgC coating powders exhibit flocculent structure with quite fine and homogeneous internal rnicropores.XRD implies that the average crystalline size of silver in coating powders is about 50 nm. The mechanical and physical properties of this newly developed AgC contact made from the above-mentioned nanocrystalline powders by traditional powder metallurgy technique were measured. Compared with its counterparts made from other techniques, the properties of this new AgC contact have been optimized. High sm-face energy and high-energy interfaces of the nanocrystalline AgC coating powders provide powerful driving force for sintering densification. Moreover, the flocculent structure of the powders is also an important factor to acquire fine density ratio.

参考文献

[1] Lambert C;Cambon G.The influence of manufacture conditions and metallurgical characteristics on the electrical behavior of silver-graphite contact materials[A].Chicago,IL,1978
[2] Wingert P.C.;Allen S.E. .The effects of graphite particle size and processing on the performance of silver-graphite contacts[J].IEEE transactions on components, hybrids, and manufacturing technology,1992(2):154-159.
[3] Wingert P.The effects of interrupting elevated currents on the erosion and structure of silver-graphite[A].Chicago,IL,1996
[4] Behrens V;Mahle E;Michal R;Saeger K.E.An advanced silver/graphite contact material based on graphite fiber[A].Loghborough,1992:185.
[5] 李秀勇,王亚平,丁秉钧.微晶、纳米晶CuCr触头材料的组织及性能[J].稀有金属,1999(05):362-365.
[6] TOUSIMI K;Yavari A.R;Ahn J.H;Sulpice A .Microstructure and hardness of Cu and Ag-based compacts with immiscible elements[J].Materials Science Forum,1999,307:223.
[7] Zheng F Q;Xie M;Liu J.L;Lv X.Y .Mechanical alloying of Ag-10Ni alloy[J].Precious Metals(in Chinese),1998,19(04):1.
[8] Wang C I;Lin S.Z;Zhao Z.L;Niu Y,Wu W.T .Microstructure of bulk nanocrystalline Ag50Ni50 alloy prepared by hot pressing of mechanical alloyed powders[J].The Chinese J Nonferrous Metals(in Chinese),2001,11(05):741.
[9] Lee G G;Toshiyuki O;Koji H .Synthesis of SnO2 panicle dispersed Ag alloy by mechanical alloying[J].Journal of the Japan Society of Powder and Powder Metallurgy,1996,43(06):795.
[10] Vinaricky E;Behrens V.Switching behavior of silver/graphite contact material in different atmospheres in regard to contact erosion[A].Arlington Va,1998
[11] Zhang W S .Overseas general situation of electrical contact materials[J].Electrical Alloy(in Chinese),1995,1:1.
[12] Yan S Q;Xu S.F;Feng Y .Fabrication of carbon fiber/metal manix composites and its application in electrical contact materials[J].Materials Science and Engineering,1998,16(01):72.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%