以氮化硅为基体,通过加入一定量的纳米碳粉等添加剂,成功的制备出了具有高强度和较高气孔率的氮化硅多孔陶瓷.采用阿基米得法、三点弯曲法测试了材料的密度、气孔率及强度;用X射线衍射仪及扫描电镜对相组成及断口进行了研究.实验结果表明:加入的纳米碳粉同在Si3N4表面的SiO2或者同Si3N4颗粒本身反应,生成了极细的SiC颗粒,钉扎在β型氮化硅的晶界,可以有效的增加材料的强度.在含碳量为5%(质量分数),1 780℃下保温60 min,可以制得强度大于100 MPa,气孔率大于40%的氮化硅多孔陶瓷.
参考文献
| [1] | Saggio-Woyansky J;Scott C E;Minnear W P .Processing of Porous Ceramics[J].American Ceramic Society Bulletin,1992,71:1674-1682. |
| [2] | 李月琴.[J].陶瓷工程,2000(12):44-47. |
| [3] | Akimune Y .High Strength SiC-particle/Si3N4 Composite[J].Nippon Seramikkusu Kyokai Gakujutsu Ronbunshi/Journal of the Ceramic Society of Japan,1990,98:424. |
| [4] | 王红洁,王永兰,金志浩.不同介质中Si3N4陶瓷的静疲劳与循环疲劳[J].稀有金属材料与工程,2003(08):639-642. |
| [5] | Xoshi Akimune;Naoto Hirosaki;Toshio Ogasawapa.Mechanical Properties of SiC-particle/Sialon Composites[J].Journal of Materials Science Letters,1991:2-23. |
| [6] | Yoshio Akimune et al.Influence of Starting Powder Characteristics on Mechanical Properties of SiC-particle/Si3N4Composites[J].Journal of the Ceramic Society of Japan,1992,100(04):463. |
| [7] | 张国军 .[J].硅酸盐学报,1993,23(06):545. |
| [8] | Heinrich J;Backer E;Bohmer M .[J].Journal of the American Ceramic Society,1988,71(01):23-28. |
| [9] | 倪国年.自韧化氮化硅陶瓷研究[J].北京理工大学学报,1996(04):380. |
| [10] | 罗学涛;张立同 .[J].复合材料学报,1997,14(03):4. |
| [11] | Pyzik A J;Beaman D R .[J].Journal of the American Ceramic Society,1990,73:244-245. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%