利用Gleeble-1500D热模拟试验机对Cu-Cr-Zr-Y合金进行高温等温压缩试验,变形温度和应变速率分别为650~850℃和0.001 ~10 s-1,对合金高温热压缩过程中的变形行为进行研究.结果表明:其流变应力随应变速率的提高而增大,随变形温度的升高而减小.并根据动态材料模型绘制和分析了该合金的热加工图,得出了热变形过程的最佳工艺参数为:温度为800~850℃,应变速率范围为0.001 ~0.1 s-1.

参考文献

[1] 快速凝固Cu-Cr-Zr-Mg合金的时效析出与再结晶[J].中国有色金属学报,1999(02):241.
[2] 赵冬梅,董企铭,刘平,康布熙,黄金亮,田保红,金志浩.Cu-3.2Ni-0.75Si合金时效早期相变规律及强化机理[J].中国有色金属学报,2002(06):1167-1171.
[3] Chengdong Xia;Yanlin Jia;Wan Zhang;Ke Zhang;Qiyi Dong;Genying Xu;Mingpu Wang .Study of deformation and aging behaviors of a hot rolled-quenched Cu-Cr-Zr-Mg-Si alloy during thermomechanical treatments[J].Materials & design,2012(Aug.):404-409.
[4] Suzuki S;Shibutani N;Minura K et al.Improvement in strength and electrical conductivity of CuNiSi alloy by aging and cold rolling[J].Journal of Alloys and Compounds,2006,417:116-120.
[5] 毕莉明,刘平,陈小红,刘新宽,李伟,马凤仓.Cu-15%Cr-0.24%Zr合金的相分析[J].中国有色金属学报(英文版),2013(05):1342-1348.
[6] 马旭,王顺兴,刘勇,王姗姗.变形量对Cu-Cr-Zr合金等温时效动力学的影响[J].热加工工艺,2009(08):10-12.
[7] Jayakumar, P.K.;Balasubramanian, K.;Rabindranath Tagore, G..Recrystallisation and bonding behaviour of ultra fine grained copper and Cu-Cr-Zr alloy using ECAP[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2012:7-13.
[8] P. Hanzelka;V. Musilova;T. Kralik;J. Vonka .Thermal conductivity of a CuCrZr alloy from 5 K to room temperatures[J].Cryogenics,2010(11/12):737-742.
[9] 董企铭,苏娟华,刘平,李贺军,康布熙.Cu-Cr-Zr-Mg合金时效析出研究[J].材料热处理学报,2004(03):38-41.
[10] Zhang L;Li Z;Lei Q et al.Hot deformation behavior of Cu-8.0Ni-l.8Si-0.15Mg alloy[J].Materials Science and Engineer A,2011,528(3):1641-1647.
[11] Correia J B;Davies H A;Sellars C M .Strengthening in rapidly solidified age hardened CuCr and CuCrZr alloys[J].Acta Materialia,1997,45(1):177-190.
[12] Mu S G;Guo F A;Tang Y Q et al.Study on the microstructure and properties of the aged Cu-Cr-Zr-Mg-RE alloy[J].Materials Science and Engineer A,2008,475(1/2):235-240.
[13] Z. Gronostajski .The deformation processing map for control of microstructure in CuAl9.2Fe3 aluminium bronze[J].Journal of Materials Processing Technology,2002(0):119-124.
[14] Momeni, A.;Dehghani, K. .Characterization of hot deformation behavior of 410 martensitic stainless steel using constitutive equations and processing maps[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2010(21/22):5467-5473.
[15] Prasad Y V R K;Rao K P .Processing maps for hot deformation of rolled AZ31 magnesium alloy plate:Anisotropy of hot workability[J].Materials Science and Engineer A,2012,487(1/2):316-327.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%