The microstructures and mechanical properties of Cr13 super martensitic stainless steel after different heat treatments were studied. The results show that the structures of the steel after quenching are of lath martensite mixed with a small amount of retained austenite. With the raising quenching temperature, the original austenite grain size increases and the lath martensite gradually becomes thicker. The structures of the tempered steel are mixtures of tempered martensite and reversed austenite dispersed in the martensite matrix. The amount of reversed austenite is from 7.54% to 22. 49%. After different heat treatments, the tensile strength, the elongation and the HRC hardness of the steel are in the range of 813 1 070 MPa, 10.1%--21.2% and 21.33--32.37, respectively. The steel displays the best comprehensive mechanical properties after the sample is quenched at 1 050 ℃ followed by tempering at 650 ℃.
参考文献
| [1] | 白鹤,王伯健.马氏体不锈钢成分、工艺和耐蚀性的进展[J].特殊钢,2009(02):30-33. |
| [2] | 徐增华.金属耐蚀材料[J].腐蚀与防护,2001(01):46-48. |
| [3] | 马明朗,杨进英,吴秀菊.马氏体不锈钢的焊接[J].水利电力机械,2004(03):29-30. |
| [4] | ZHANG Xiaokfu.Super Martensitic Stainless Steel[J].Tai-Gang Translation,1999(04):66. |
| [5] | LUO Su-juan.Study on Reserved Austenite in 00Crl5Ni6Mo2A1Nb[J].Aerospace Materials & Technology,1982(06):34. |
| [6] | 方旭东,张寿禄,杨常春,夏焱,赵建伟.TGOG13Cr-1超级马氏体不锈钢的组织和性能[J].钢铁,2007(08):74-77. |
| [7] | CHEN Cheng da;LIU Zheng.Improvement of Structure and Property on ZGOCr13Ni4-6 Martensitic Stainless Steels[J].Heavy Castings and Forgings,1987(02):40. |
| [8] | 易邦旺,钱学君.镍含量对13Cr型低碳马氏体不锈钢性能的影响[J].金属功能材料,1997(02):75. |
| [9] | MA Xun .Effect of Heat Treatment on Structure and Properties of Martensite Stainless Steel 0Crl3Ni4Mo[J].Special Steel,1995,16(05):19. |
| [10] | LI Xiao-yu;WANG Ya;DU Bing.Effect of Retained Austenite Formed During Postweld Heat Treatment on Fracture Toughness of Deposited Metal of 0Crl3Ni5Mo[J].Welding Journal,2007(10):47. |
| [11] | LU Shi ying;ZHANG Ting-kai;KANG Xi-fan.Stainless Steel[M].北京:原子能出版社,1995 |
| [12] | JIANG Yue.Alloying Design and Microstructure and Property of Maraging Stainless Steel[M].哈尔滨:哈尔滨工业大学出版社,2007 |
| [13] | YONG Qi-long.Secondary Phases in Steels[M].北京:冶金工业出版社,2006 |
| [14] | 周倩青,雍兴平,李秀艳,翟玉春.沉淀硬化FV520B钢的低温性能研究[J].腐蚀科学与防护技术,2009(03):299-301. |
| [15] | 王培,陆善平,李殿中,康秀红,李依依.低加热速率下ZG06Cr13Ni4Mo低碳马氏体不锈钢回火过程的相变研究[J].金属学报,2008(06):681-685. |
| [16] | WEN He .Formation Mechanism of Reversed Austenite in Low Carbon Martensitic Stainless Steel[J].Steel Pipe,2004,33(06):66. |
| [17] | Eun Seo Park;Dae Kyoung Yoo;Jee Hyun Sung .Formation of Reversed Austenite during Tempering of 14Cr-7Ni-0.3Nb-0.7Mo-0.03C Super Martensitic Stainless Steel[J].Metals and Materials International,2004(6):521-525. |
| [18] | Dong-Seok Leem;Yong-Deuk Lee;Joong-Hwan Jun .Amount of retained austenite at room temperature after reverse transformation of martensite to austenite in an Fe-13 percent Cr-7 percent Ni-3 percent Si martensitic stainless steel[J].Scripta materialia,2001(7):767-772. |
| [19] | G. ROZNOVSKA;V. VODAREK;A. KORCAK .THE EFFECT OF HEAT TREATMENT ON MICROSTRUCTURE AND PROPERTIES OF A 13Cr6Ni2.5Mo SUPERMARTENSITIC STEEL[J].Vysoka Skola Banska Sbornik Vedeckych Praci: Rada Hutnicka.,2005(1):225-231. |
| [20] | 刘振宝,杨志勇,梁剑雄,张秀丽.超高强度马氏体时效不锈钢中逆转变奥氏体的析出与长大行为[J].金属热处理,2010(02):11-15. |
| [21] | LIU Zhen-bao;YANG Zhi-yong;LIANG Jian-xiong et al.Precipitation Behavior and Transformation Kinetics of Rever ted Austenite in High-Strength Stainless Steel[J].Transactions of Materials and Heat Treatment,2010,31(06):39. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%