为了提高胶原溶液的粘弹性能和热稳定性,以及提高胶原耐酶解的能力,使用一种新的交联剂--N-羟基琥珀酰亚胺己二酸酯(NHS-AA),对胶原溶液进行交联改性.动态流变仪测定结果表明,在f=0.02Hz和25℃时,胶原溶液的弹性模量(G'),粘性模量(G")和复数粘度(η*)分别从未交联时的0.03、0.11Pa和0.76Pa·s增加到22.83、3.36Pa和143.90Pa·s.差示扫描量热分析仪(DSC)测量结果显示,交联后胶原溶液的热变性温度达到42.5℃,比未交联胶原溶液(40.4℃)提高了2.1℃.针对交联后胶原溶液制成的海绵,电泳法(SDS-PAGE)研究表明胶原海绵抗酶降解能力显著增强.
参考文献
| [1] | 任俊莉,付丽红,邱化玉.胶原蛋白的应用及其发展前景[J].中国皮革,2003(23):16-17. |
| [2] | 公维菊,李国英.胶原交联改性的研究现状[J].皮革化工,2007(05):21-25,30. |
| [3] | Saito H;Taguchi T;Aoki H;Murabayashi S;Mitamura Y;Tanaka J;Tateishi T .pH-responsive swelling behavior of collagen gels prepared by novel crosslinkers based on naturally derived di- or tricarboxylic acids.[J].Acta biomaterialia,2007(1):89-94. |
| [4] | 王迎军,杨春蓉,汪凌云.EDC/NHS交联对胶原物理化学性能的影响[J].华南理工大学学报（自然科学版）,2007(12):66-70,96. |
| [5] | Zeeman R;Dijkstra PJ;van Wachem-PB;van Luyn-MJ;Hendriks M;Cahalan PT;Feijen J .Successive epoxy and carbodiimide cross-linking of dermal sheep collagen.[J].Biomaterials,1999(10):921-931. |
| [6] | Sheu MT;Huang JC;Yeh GC;Ho HO .Characterization of collagen gel solutions and collagen matrices for cell culture.[J].Biomaterials,2001(13):1713-1719. |
| [7] | Bigi A;Panzavolta S;Rubini K .Relationship between triple-helix content and mechanical properties of gelatin films.[J].Biomaterials,2004(25):5675-5680. |
| [8] | Ma L;Gao C;Mao Z;Zhou J;Shen J .Enhanced biological stability of collagen porous scaffolds by using amino acids as novel cross-linking bridges.[J].Biomaterials,2004(15):2997-3004. |
| [9] | Iwata H;Matsuda S;Mitsuhashi K;Itoh E;Ikada Y .A novel surgical glue composed of gelatin and N-hydroxysuccinimide activated poly(L-glutamic acid): Part 1. Synthesis of activated poly(L-glutamic acid) and its gelation with gelatin.[J].Biomaterials,1998(20):1869-1876. |
| [10] | Saito H;Taguchi T;Kobayashi H et al.[J].Materials Science and Engineering C:Biomimetic and Supramolecular Systems,2004,24:781-785. |
| [11] | Aoki H;Taguchi T;Saito H et al.[J].Materials Science and Engineering C:Biomimetic and Supramolecular Systems,2004,24:787-790. |
| [12] | Taguchi T;Saito H;Uchida Y et al.[J].Materials Science and Engineering C:Biomimetic and Supramolecular Systems,2004,24:775-780. |
| [13] | Taguchi T;Saito H;Aoki H et al.[J].Materials Science and Engineering C:Biomimetic and Supramolecular Systems,2006,26:9-13. |
| [14] | 李季衡,李洋,李国英.戊二醛对胶原溶液热稳定性的影响[J].皮革科学与工程,2009(01):14-17,26. |
| [15] | Kasapis S;Mitchell J R .[J].International Journal of Biological Macromolecules,2001,29:315-321. |
| [16] | Korhonen M;Hellen L;Hirvonen J;Yliruusi J .Rheological properties of creams with four different surfactant combinations - effect of storage time and conditions.[J].International Journal of Pharmaceutics,2001(1/2):187-196. |
| [17] | Achet D.;He XW. .DETERMINATION OF THE RENATURATION LEVEL IN GELATIN FILMS[J].Polymer,1995(4):787-791. |
| [18] | Chen RN;Ho HO;Sheu MT .Characterization of collagen matrices crosslinked using microbial transglutaminase.[J].Biomaterials,2005(20):4229-4235. |
| [19] | Li, Y;Li, YW;Du, ZL;Li, GY .Comparison of dynamic denaturation temperature of collagen with its static denaturation temperature and the configuration characteristics in collagen denaturation processes[J].Thermochimica Acta,2008(1/2):71-76. |
| [20] | 李洋,李艳稳,杜宗良,李国英.剪切作用对胶原热稳定性能的影响[J].中国皮革,2007(17):12-15. |
| [21] | Sajithlal G B;Chithra P;Chandrakasan G .[J].Biochrimica et Biophysica Acta,1998,1407:215-224. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%