以Na2CO3·10H2O和NaOH混合碱为沉淀剂,采用共沉淀法制备了钙钛矿型结构的La1-x-yBaxREyMnO3(RE=Dy或Y)复合氧化物超细粒子.该复合氧化物超细粒子具有较大的比表面积和良好的热稳定性(经700和1000 ℃焙烧后,其比表面积仍分别可达到47.0和16.9 m2/g).随着LaMnO3中的La3+被Ba2+及稀土离子Dy3+或Y3+部分取代后,样品显示出良好的热稳定性及对甲烷燃烧的高催化活性.
参考文献
[1] | Cui X L;Liu Y .[J].Chemical Engineering Journal,2000,78(2/3):205. |
[2] | Choudhary V R;Banerjee S;Uphade B S .[J].Applied Catalysis A:General,2000,197(02):L183. |
[3] | Liu Y;Zheng H T;Liu J R;Zhang T .[J].Chemical Engineering Journal,2002,89(1-3):213. |
[4] | Teraoka Y.;Kagawa S.;Jansson K.;Nygren M.;Nii H. .Influence of the simultaneous substitution of Cu and Ru in the perovskite-type (La,Sr)MO3 (M=Al, Mn, Fe, Co) on the catalytic activity for CO oxidation and CO-NO reactions[J].Applied Catalysis, A. General: An International Journal Devoted to Catalytic Science and Its Applications,2000(Special Issue SI):35-41. |
[5] | Ma J X;Fang M;Lau N T .[J].Applied Catalysis A:General,1997,150(02):253. |
[6] | Ichimura K;Inoue Y;Yasumori I .[J].Catalysis Review-Science and Engineering,1992,34(04):301. |
[7] | Liu Y;Zheng H T;Liu Q Sh .[J].Reaction Kinetics and Catalysis Letters,2002,76(01):27. |
[8] | Kirchnerova J;Klvana D;Vaillancourt J;Chaouki J .[J].Catalysis Letters,1993,21(1/2):77. |
[9] | Lee Y N;Sapina F;Martinez E;Folgado J V, Corberan V C .[J].Studies in Surface Science and Catalysis,1997,110:747. |
[10] | Saracco G;Geobaldo F;Baldi G .[J].Applied Catalysis B:Environmental,1999,20(04):277. |
[11] | Fierro J L G .[J].Catalysis Today,1990,8(02):153. |
[12] | Petunchi J O;Lombardo E A .[J].Catalysis Today,1990,8(02):201. |
[13] | Ciambelli P;Cimino S;De Rossi S;Faticanti M,Lisi L,Minelli G,Pettiti I,Porta P,Russo G,Turco M .[J].Applied Catalysis B:Environmental,2000,24(3/4):243. |
[14] | YANG Huanghe,ZHANG Tao,TIAN Hanjing,XU Dezhu,TANG Junwang,LIN Liwu.Decomposition of High Concentration Hydrogen Peroxide over Alumina-Supported Lao.6Sr0.4MnO3 Perovskite Catalyst[J].催化学报,2001(03):225-226. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%