选用ZnSO4和MgSO4两种电沉积溶液,对带裂缝的砂浆试件进行修复,测定了7天、14天、21天、28天、35天龄期带裂缝砂浆试件无裂缝处及裂缝处的碳化深度,研究了带裂缝的砂浆试件经过电沉积处理后碳化深度的变化情况.结果表明:利用ZnSO4和MgSO4两种电沉积溶液,对带裂缝的砂浆试件进行电沉积处理后,其抗碳化能力均有所提高,而且采用MgSO4溶液,抗碳化能力的提高程度要高于采用ZnSO4溶液的.
参考文献
| [1] | Otsuki N;Hisada M;Ryu J S et al.Rehabilition of concrete cracks by electrodeposition[J].Concrete International,1999,21(03):58. |
| [2] | Otsuki N;Ryu J S .Use of electrodeposition for repair of concrete with shrinkage cracks[J].Journal of Materials in Civil Engineering,2001,13(02):136. |
| [3] | Ryu J S .An experimental study on the repair of concrete crack by electrochemical technique[J].Materials and Structures,2001,34(04):433. |
| [4] | Jae-Suk Ryu;Nobuaki Otsuki .Crack closure of reinforced concrete by electrodeposition technique[J].Cement and Concrete Research,2002(1):159-164. |
| [5] | 储洪强;蒋林华;徐金霞 .钢筋混凝土电沉积修复技术研究[J].混凝土与水泥制品,2004,136(ZK):25. |
| [6] | 储洪强,蒋林华.利用电沉积方法修复混凝土裂缝试验研究[J].河海大学学报（自然科学版）,2005(03):310-313. |
| [7] | 蒋林华,储洪强.混凝土参数对沉积效果的影响[J].水利水电科技进展,2005(02):23-25. |
| [8] | 储洪强,蒋林华,华卫兵.辅助电极及电极距离对沉积效果的影响[J].建筑材料学报,2005(04):456-461. |
| [9] | 储洪强 .电沉积方法修复混凝土裂缝技术研究[D].河海大学,2005. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%