采用拉伸性能测试、显微硬度测试、扫描电镜和透射电镜观察等手段,研究了不同时效温度对50%冷变形2519A铝合金组织和力学性能的影响.结果表明:采用较大变形程度(50%)冷轧,再进行低温较长时间时效(140℃×6 h),可使2519A铝合金的强度得到显著提高(σb=551 MPa),同时其伸长率不低于7%;经冷变形的2519A铝合金,在稍高温度短时间(190℃×2 h)时效处理,将导致时效强化能力降低,但仍不低于常规时效处理(T6态:170℃×13 h).
参考文献
| [1] | James J. Fisher Jr.;Lawrence S. Kramer;Joseph R. Pickens .ALUMINUM ALLOY 2519 IN MILITARY VEHICLES[J].Advanced Materials & Processes,2002(9):43-46. |
| [2] | Devicent S M;Devletian J H;Gedon S A .Weld properties of the newly developed 2519-T87 aluminum armor alloy[J].Welding Journal,1988,67(07):33-43. |
| [3] | Stanilaw Dymek;Marek Dollar .TEM investigation of age-hardenable Al 2519 alloy subjected to stress corrosion cracking tests[J].Materials Chemistry and Physics,2003,82(01):1-3. |
| [4] | Sugamata M;Kaneko J .Effect of thermomechanical treatment on mechanical properties of 2024 aluminum alloy[J].Light Metals,1983,33(07):407-414. |
| [5] | 王祝堂;田荣璋.铝合金及其加工手册[M].长沙:中南大学出版社,2000:103-108. |
| [6] | 李松瑞;周善初.金属热处理[M].长沙:中南大学出版社,2003 |
| [7] | Singh S;Goel D B .Influence of thermomechanical aging on tensile properties of 2014 aluminium alloy[J].Materials Science,1990,25:3894-3900. |
| [8] | 李慧中,梁霄鹏,陈明安,张新明.冷轧变形量对2519铝合金组织与力学性能的影响[J].材料热处理学报,2008(02):86-89. |
| [9] | Mondolfo L F.Aluminum Alloys:Structure and Properties[M].London:butterworth,1976:97. |
| [10] | 戚正风.固态金属中的扩散与相变[M].北京:机械工业出版社,1998 |
| [11] | 宁爱林,刘志义,曾苏民.大冷变形对2024铝合金组织和性能的影响[J].金属热处理,2006(09):22-24. |
| [12] | 王建华,易丹青,陈康华.形变热处理对2618铝合金性能的影响[J].热加工工艺,2001(02):13-14. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%