为提高碳纤维／环氧树脂复合材料的界面粘结性能，采用7射线共辐照接枝方法对碳纤维表面改性，利用X光电子能谱仪（XPS）、扫描电子显微镜（SEM）、电子万能材料试验机，研究了在缩乙二醇丙酮溶液和环氧氯丙烷丙酮溶液中经200kGy剂量的Υ射线辐照接枝后，碳纤维的表面化学元素及官能团组成、表面形貌、复合材料剪切断面形貌及其层间剪切强度（ILSS）的变化。研究表明，缩乙二醇类接枝液的接枝效果较理想，碳纤维接枝率达7％；辐照处理碳纤维表面O／C比值和含氧官能团含量增加，以此制备的碳纤维／环氧复合材料的ILSS提高，最大提高率达31．2％；同时还发现辐照接枝后的碳纤维表面粗糙度增大。
Υ-ray total irradiation inducing grafting was used to modify the carbon fiber surface to improve interfaeial adhesion properties of the carbon fiber/epoxy composite. The change of surface chemical elements and functional groups composition, surface morphology, fracture surface and interIaminar shear strength （ILSS） of the carbon fiber/epoxy composite after 200 kGy doses of Υ- ray radiation in different grafting solutions were studied severally with XPS,SEM,and electronic universal testing machine. The results show that condensed ethylene glycol graft solutions have ideal grafting effect, the carbon fiber grafting rate is 7%. the surface O/C ratio and the content of oxygen functional groups is increased, the ILSS of irradiated carbon fiber/epoxy composite also is increased, the maximum ILSS is increased by the rate of 31. 2%. The surface roughness of carbon fiber is increased after irradiation.
参考文献
| [1] | Xu Zhiwei,Huang Yudong,Zhang Chunhua,et al.Effect of γ-ray irradiation grafting on the carbon fibers and interfacialadhesion of epoxy composites[J].Composites Science andTechnology,2007,67(15/16):3261-3270. |
| [2] | 朱黎黎,张佐光,李敏,等.工艺温度下树脂与纤维的接触角及其粘附作用研究[J].复合材料学报,2010,27(5):41-46. |
| [3] | 高鑫,宋艳江,王晓东,等.复合处理碳纤维增强聚酰亚胺复合材料力学性能[J].复合材料学报,2009,26(3):50-54. |
| [4] | Cao H,Huang Y,Zhang Z,et al.Uniform modification of carbon fibers surface in 3-D fabrics using intermittentelectrochemical treatment[J].Compos Sci Technol,2005,65(11/12):1655-1662. |
| [5] | Li J.Interfacial studies on the O3modified carbon fiber-reinforced polyamide 6composites[J].Appl Surf Sci,2008,255(5):2822-2824. |
| [6] | Seo M,Park S.Surface characteristics of carbon fibersmodified by direct oxyfluorination[J].J Colloid Interface Sci,2009,330(1):237-242. |
| [7] | 宋艳江,高鑫,朱鹏,等.表面处理碳纤维增强聚酰亚胺复合材料力学性能[J].复合材料学报,2008,25(5):64-68. |
| [8] | 贺福,王润娥.用气相氧化法对碳纤维进行表面处理[J].复合材料学报,1988,5(1):56-61. |
| [9] | 刘玉文,张志谦,李凤梅,等.高能电子束辐照对碳纤维表面结构的影响[J].辐射研究与辐射工艺学报,2002,20(3):197-203. |
| [10] | Montes-Morn M A,Martínez-Alonso A,Tascón J M D,etal.Effects of plasma oxidation on the surface and interfacialproperties of ultra-high modulus carbon fibres[J].Composites Part A,2001,32(3/4):361-371. |
| [11] | Barletta M,Gisario A.Electrostatic spray painting of carbonfiber-reinforced epoxy composites[J].Prog Org Coat,2009,64(4):339-349. |
| [12] | Xu B,Wang X,Lu Y.Surface modification ofpolyacrylonitrile-based fiber and its interaction with imide[J].Appl Surf Sci,2006,253(5):2695-2701. |
| [13] | Singh A.Radiation processing of carbon fibre-reinforcedadvanced composites[J].Nucl Instrum Methods Phys Res B,2001,185(1-4):50-54. |
| [14] | Clough R L.High-energy radiation and polymers:A review of commercial processes and emerging applications[J].Nucl Instrum Methods Phys Res B,2001,185(1-4):8-33. |
| [15] | Li Junqing,Huang Yudong,Fu Shaoyun,et al.Study on thesurface performance of carbon fibres irradiated by g-ray underdifferent irradiation dose[J].Applied Surface Science,2010,256(7):2000-2004. |
| [16] | 马恒怡,黄玉东,张志谦,等.^60Coγ-辐射接枝对粘胶基碳纤维的表面改性[J].材料科学与工艺,2003,11(2):172-175. |
| [17] | 李峻青,徐用军,张怀志.γ射线辐照对碳纤维及其复合材料力学性能的影响[J].合成纤维,2006(11):20-23. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%