利用熔体快淬法和晶化退火处理工艺制备纳米晶复合NdFeB永磁合金,研究添加Co和Zr元素对合金晶化行为、微结构和磁性能的影响.结果表明,添加Co元素降低了晶化相的析出温度,提高了合金的剩磁；进一步增加Zr元素后,合金的晶化行为由两步晶化变为软硬磁相同步析出,合金的矫顽力明显提高,晶粒得到细化,软、硬磁相之间的交换耦合作用显著增强,从而使合金Nd9.5Fe76Co5Zr3B6.5表现出优异的综合磁性能,即Jr=0.93 T,iHc=687 kA/m,(BH)max=129 kJ/m3.
参考文献
| [1] | Coehoorn R;Mooij de B;Buschow K et al.[J].Journal of Physics C:Solid State Physics,1988,8:669. |
| [2] | Liu Z W;Davies A H .[J].Journal of Magnetism and Magnetic Materials,2005,290:1230. |
| [3] | Yang S;Song X P;Gu B X et al.[J].Journal of Alloys and Compounds,2005,394:1. |
| [4] | Chang WC.;Chang JK.;Chang HW.;Chen SK. .Magnetic properties and phase evolution of nanocomposite Nd10Febal.MCB10.5 (M = Ti, Nb, V, Cr and Mo) melt-spun ribbons[J].Physica, B. Condensed Matter,2003(2/4):296-299. |
| [5] | Skomski R;Coey J .[J].Physical Review B:Condensed Matter,1993,48:15812. |
| [6] | 王晨,文玉华,严密.Nb和Zr对（Nd,Pr）2Fe14B/α-Fe磁体晶化行为和磁性能的影响[J].稀有金属材料与工程,2005(11):1782-1785. |
| [7] | 刘锦云,查五生,陈德波,涂铭旌.Nb元素对纳米晶（Nd,Pr）FeB/α-Fe复合永磁合金显微结构与磁性能的影响[J].稀有金属材料与工程,2007(11):1987-1990. |
| [8] | Bai F M;Jiang Zh L;Chen X Y et al.[J].dAlloy Compd,2002,343:60. |
| [9] | Grady K;Hilo M;Chantrell R .[J].IEEE Transactions on Magnetics,1993,29:2608. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%