在紫铜上直接喷涂的金属钨(W)层容易出现早期剥落.采用低压等离子体技术制备了Ni-Cu底层、Ni-W中间层和W层;利用大功率CO2激光束对W涂层重熔,研究了激光重熔处理对W涂层显微组织、致密度、结合强度及显微硬度的影响.结果表明:低压等离子喷涂的W层主要呈层状结构,W颗粒熔化不充分,涂层中存在大量的孔洞等缺陷;激光重熔后,W涂层表面的W颗粒已完全熔化,并在激光冷效应的作用下形成了一层厚度约为300μm的细晶组织,W涂层的致密度、结合强度得到了明显的提高.
参考文献
| [1] | 种法力,陈俊凌,李建刚.VPS-EBW法制备W/Cu功能梯度材料及热负荷实验研究[J].稀有金属材料与工程,2006(09):1509-1512. |
| [2] | 刘翔,谌继明,许增裕,邓颖,葛昌纯,李江涛.W/Cu梯度功能材料的高热负荷性能研究[J].核聚变与等离子体物理,2002(04):203-208. |
| [3] | G. Pintsuk;S.E. Bruenings;J.-E. Doering;J. Linke;I. Smid;L. Xue .Development of W/Cu―functionally graded materials[J].Fusion engineering and design,2003(0):237-240. |
| [4] | Wang TG;Chen JL;Chen Y;Wu YC .Thermal properties of VPS-W coatings on CuCrZr alloy with Ti bonding layer[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2007(0):1294-1298. |
| [5] | Riccardi B;Montanari R;Casadei M;Costanza G;Filacchioni G;Moriani A .Optimisation and characterisation of tungsten thick coatings on copper based alloy substrates[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2006(1/3):29-35. |
| [6] | 刘翔,谌继明,许增裕,邓颖,葛昌纯,李江涛,田树贤,吉田直亮.W/Cu和W/C涂层的循环热负荷实验[J].核科学与工程,2003(02):139-144. |
| [7] | 简中华,马壮,王富耻,曹素红.热喷涂铜基W涂层工艺性能研究[J].兵器材料科学与工程,2007(02):27-30. |
| [8] | 种法力,陈俊凌,李建刚.铜基体上爆炸喷涂钨涂层及其电子束热负荷实验研究[J].表面技术,2005(06):33-34,37. |
| [9] | R. Neu;R. Dux;A. Geier;O. Gruber;A. Kallenbach;K. Krieger;H. Maier;R. Pugno;V. Rohde;S. Schweizer .Tungsten as plasma-facing material in ASDEX Upgrade[J].Fusion engineering and design,2003(3):367-374. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%