采用自动氩弧焊,选用不同焊接工艺对T92和S30432异种钢进行了焊接,研究了异种钢接头中δ铁素体的分布情况以及焊接工艺变化对δ铁素体含量的影响.结果表明:T92/S30432异种钢接头熔合区存在块状的δ铁素体,其性质是合金铁素体,沿熔合区方向呈带状分布,且在焊接接头上不均匀分布,焊接接头底部和表面区域δ铁素体含量高、尺寸大,其他区域极少;ERNiCrMo-3焊丝和小坡口角度下异种钢接头中δ铁素体含量较高,其他焊接工艺参数变化(层间温度、焊接层数、热处理温度)对δ铁素体含量影响较小.
参考文献
| [1] | Hasti S;Aroonwilas A;Veawab A .Exergy analysis of ultra super-critical power plant[J].Energy Procedia,2013,37:2544-2551. |
| [2] | SHI Ru-xing,LIU Zheng-dong.Hot Deformation Behavior of P92 Steel Used for Ultra-Super-Critical Power Plants[J].钢铁研究学报：英文版,2011(07):53-58. |
| [3] | 殷尊,蔡晖,刘鸿国.1000MW超超临界机组用P92耐热钢高温服役后的性能[J].材料热处理学报,2012(11):105-110. |
| [4] | 宋有明,陈国宏,余新海,刘俊建,王家庆,化建,张涛,张建华,汤文明.T92/HR3C异种钢焊接接头高温拉伸变形及断裂行为[J].材料热处理学报,2012(02):72-78. |
| [5] | Guohong Chen;Qi Zhang;Junjian Liu;Jiaqing Wang;Xinhai Yu;Jian Hua;Xiaolong Bai;Tao Zhang;Jianhua Zhang;Wenming Tang .Microstructures and mechanical properties of T92/Super304H dissimilar steel weld joints after high-temperature ageing[J].Materials & design,2013(Feb.):469-475. |
| [6] | Yan Gao;Chunlei Zhang;Xiahua Xiong.Intergranular corrosion susceptibility of a novel Super304H stainless steel[J].Engineering failure analysis,2012:26-32. |
| [7] | Jian Cao;Yi Gong;Zhen-Guo Yang;Xiao-Ming Luo;Fu-Ming Gu;Zheng-Fei Hu .Creep fracture behavior of dissimilar weld joints between T92 martensitic and HR3C austenitic steels[J].International Journal of Pressure Vessels and Piping,2011(2/3):94-98. |
| [8] | Gong, Y.;Cao, J.;Ji, L.-N.;Yang, C.;Yao, C.;Yang, Z.-G.;Wang, J.;Luo, X.-M.;Gu, F.-M.;Qi, A.-F.;Ye, S.-Y.;Hu, Z.-F. .Assessment of creep rupture properties for dissimilar steels welded joints between T92 and HR3C[J].Fatigue & Fracture of Engineering Materials and Structures,2011(2):83-96. |
| [9] | 郑子杰,田志豪,王崇斌,孙锋.T92/HR3C异种钢接头热影响区内高温铁素体的试验分析[J].锅炉技术,2013(04):52-55. |
| [10] | 刘俊建,陈国宏,余新海,王家庆,化建,宋有明,张涛,汤文明.T92/HR3C异种钢焊接接头的组织结构和力学性能[J].材料热处理学报,2011(02):54-60. |
| [11] | 陈国宏,余新海,刘俊建,王家庆,化建,宋有明,张涛,汤文明.T92/TP347H异种钢焊接接头的组织结构和力学性能[J].压力容器,2010(12):1-7. |
| [12] | 周敏,周强国,严伟,王威,樊新民,单以银.新型高硅铁素体/马氏体钢中的δ铁素体[J].钢铁,2013(05):62-67. |
| [13] | P. Wang;S.P. Lu;N.M. Xiao;D.Z. Li;Y.Y. Li .Effect of delta ferrite on impact properties of low carbon 13Cr–4Ni martensitic stainless steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2010(13/14):3210-3216. |
| [14] | Francis J A;Mazur W;Bhadeshia HKDH .Type Ⅳ cracking in ferritie power plant steels[J].Materials Science and Technology,2006,22(12):1387-1395. |
| [15] | Hsieh C C;Lin D Y;Chen M C et al.Precipitation and strengthening behavior of massive δ-ferrite in dissimilar stainless steels during massive phase transformation[J].Materials Science and Engineering A,2008,477(1-2):328-333. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%