采用燃烧合成法,以硅粉和炭黑为原料,铝粉为掺杂剂,聚四氟乙烯为助燃剂,分别在不同坯体压力下制备成坯体,在0.1MPa的氮气气氛中合成Al掺杂β-SiC粉体.通过X射线衍射、扫描电镜和电子能谱对合成粉体的物相、微观结构及形貌进行了表征.同时在8.2~12.4GHz频率范围内进行了介电性能测试.结果表明随着坯体压力的增大,合成β-SiC粉体的晶格参数随之减小,且其介电性能随之降低.对合成机理和Al掺杂对SiC介电性能的影响进行了讨论.
参考文献
[1] | Krstic V D .[J].Journal of the American Ceramic Society,1992,75(01):170-175. |
[2] | Fissel A;Schroter B;Richter W .[J].Applied Physics Letters,1995,66(32):3182. |
[3] | Zhang B;Li J B;Sun J J et al.[J].Journal of the European Ceramic Society,2002,22:93-99. |
[4] | Zhao DL.;Zhou WC.;Zhao HS. .Dielectric properties of nano Si/C/N composite powder and nano SiC powder at high frequencies[J].Physica, E. Low-dimensional systems & nanostructures,2001(4):679-685. |
[5] | 苏晓磊,周万城,李智敏,罗发,朱冬梅.低氮气压下燃烧合成Al掺杂β-SiC粉体的微波介电性能[J].稀有金属材料与工程,2009(z2):55-58. |
[6] | Narayan J;Raghunathan R;Chowdhury R et al.[J].Journal of Applied Physics,1994,75(11):7252-7257. |
[7] | Yang Kun;Yang Yun;Lin Zhiming et al.[J].Materials Research Bulletin,2007,42:1625-1632. |
[8] | Khachatryan G L;Arutyunyan A B;Kharatyan S L .[J].Combustion Explosion and Shock Waves,2006,42(05):543-548. |
[9] | Jason Shin;Do-Hwan Ahn;Mee-Shik Shin;Yong Seog Kim .Self-propagating high-temperature synthesis of aluminum nitride under lower nitrogen pressures[J].Journal of the American Ceramic Society,2000(5):1021-1028. |
[10] | Liu Guanghua;Yang Kun;Li Jiangtao et al.[J].Journal of Physical Chemistry C,2008,112:6285-6292. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%