管线钢的应力腐蚀研究现状及损伤机理

材料导报, 2001, 15(12): 1-20.

管线钢的应力腐蚀研究现状及损伤机理

方丙炎 ^1, , 韩恩厚 ^2, , 朱自勇 ^3, , 王俭秋 ^4, , 柯伟 ^5,

1.中国科学院金属研究所,

2.中国科学院金属研究所,

3.中国科学院金属研究所,

4.中国科学院金属研究所,

5.中国科学院金属研究所,

基金项目: 国家重点基础研究发展计划(973计划)(G1 9990650) 中国科学院"百人计划"

关键词：管线钢 , 应力腐蚀 , 高pH应力腐蚀开裂 , 近中性pH应力腐蚀开裂

Current State of Research on Stress Corrosion Cracking in Pipeline Steels and Damage Mechanisms

回顾了管线钢的应力腐蚀研究现状,并比较了发生在管道外的"经典型"的高pH应力腐蚀开裂与近十多年来发现和研究的近中性pH应力腐蚀开裂的特征,讨论了它们的影响因素以及开裂机理,最后展望了埋地管道的未来研究方向.

参考文献

[1]	Townsend H E Jr .[J].MP,1972,11:33.
[2]	Kentish P J .[J].British Corrosion Journal,1985,20:139.
[3]	Delanty B;O′Beirne J .[J].Oil & Gas Journal,1992,15:39.
[4]	Sutcliffe J M;Fessler R R;Boyd W K et al.[J].Corrosion,1972,28(08):313.
[5]	Parkins R N;Greenwell B S .[J].Metal Science Journal,1977,11:405.
[6]	Beavers J A;Berry W E;Parkins R N .[J].MP,1986,25(06):9.
[7]	Beavers J A;Christman T K;Parkins R N .[J].MP,1988,27(04):22.
[8]	Parkins R N .[J].Corrosion,1990,46:178.
[9]	Parkins R N;Markworth A J;Holbrook J H .[J].Corrosion,1988,44:572.
[10]	Parkins R N;Singh P M .[J].Corrosion,1990,46:485.
[11]	Christman T K .[J].Corrosion,1990,46:450.
[12]	Parkins R N;Belhimer E;Blanchard Jr W K .[J].Corrosion,1993,49:951.
[13]	Delanty B;O′Beirne J .[J].Oil & Gas Journal,1985,20:139.
[14]	Parkins R N;Blanchard Jr W K;Delanty B S .[J].Corrosion,1994,50:394.
[15]	Szklarska-Smialowska Z;Xia Z;Rebak R B .[J].Corrosion,1994,50:334.
[16]	Harle B A;Beavers J A .[J].Corrosion,1993,49:861.
[17]	Ahmed T M;Lambet S B;Sutherby R et al.[J].CORROSION,1998,54:115.
[18]	Parkins R N .[R].AGA PRC Report PR-232-9401 54,November,1994.
[19]	Wilmott M J;Jack T R;Van Boven G.[J].Corrosion,1996:242.
[20]	CEPA .Submission to the National Energy Board[J].Proceeding MH-2-95,1996,1
[21]	Barlo T J.6 th Symposium on Line Pipe Research[J].American Gas Associatio Inc,1979
[22]	Beavers J A;Harle B A.Proc 1 st intern Pipeline Conf,IPC/96[J].ASME,1996:573.
[23]	Parkins R N .[J].Journal of the Iron and Steel Institute,1952,172:149.
[24]	Parkins R N."First Symposium on Line Pipe Research[J].American Gas Association Catalogne,1974:174.
[25]	WANG J Q;Atrens A;Cousens D R et al.[J].Journal of Materials Science,1999,34:1711.
[26]	WANG J Q;Atrens A;Cousens DR et al.[J].Journal of Materials Science,1999,34:1721.
[27]	WANG J Q;Atrens A;Cousens D R et al.[J].Acta Materialia,1998,46:5677.
[28]	Cousens DR.;Wang JQ.;Atrens A.;Wood BJ. .Implications of specimen preparation and of surface contamination for the measurement of the grain boundary carbon concentration of steels using x-ray microanalysis in an UHVFESTEM[J].Surface and Interface Analysis: SIA: An International Journal Devoted to the Development and Application of Techniques for the Analysis of Surfaces, Interfaces and Thin Films,2000(1):23-32.
[29]	Beavers J A;Harle B A.Proc 1 st intern Pipeline Conf,IPC/96,ASME[C].,1996:573.
[30]	Pikey A K;Lambert S B;Plumtree A .[J].Corrosion,1995,52:91.
[31]	Harle B A;Beavers J A;Jaske C E .Corrosion/94[R].,1994.
[32]	Plumtree A;Lambert S B;Sutherby R.[J].European Federation of Corrosion Publications,1996:26.
[33]	Qiao L J;Luo J L;Mao X .[J].CORROSION,1998,54:115.
[34]	Zheng W;Macleod F A;Revie R W.[J].European Federation of Corrosion Publications,1996:28.
[35]	Plumtree A;Lambert S B;Sutherby R.[J].European Federation of Corrosion Publications,1996:26.
[36]	Schmidt G.Corrosion/83[M].,1983(03)

上一张下一张

计量

下载量()
访问量()

作者相关

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

管线钢的应力腐蚀研究现状及损伤机理

Current State of Research on Stress Corrosion Cracking in Pipeline Steels and Damage Mechanisms

参考文献