采用液面下降法在载玻片上制备了TiO2-SiO2/St-MMA共聚物复合双层光学增透膜.考察了成膜材料组成对内外膜层折射率的影响规律,研究了紫外光辐照处理对内层无机膜厚度和折射率的影响,用紫外-可见分光光度计测试了增透膜的透过率.实验结果表明各膜层折射率随其组成比的变化而线性变化,内层膜和外层膜的折射率可分别在1.45～2.0和1.49～1.60之间连续可调.制备的双层光学增透膜在420 nm～600 nm光谱范围的透过率有很大提高,最高透过率达到99.5%,最高透过波长的位置可通过膜层厚度调整.
参考文献
| [1] | Xu Y;Zhang B;Fan W H et al.[J].THIN SOLID FILMS,2003,440:180-183. |
| [2] | Bautista MC.;Morales A. .Silica antireflective films on glass produced by the sol-gel method[J].Solar Energy Materials and Solar Cells: An International Journal Devoted to Photovoltaic, Photothermal, and Photochemical Solar Energy Conversion,2003(2):217-225. |
| [3] | Vong MSW.;Sermon PA. .OBSERVING THE BREATHING OF SILICA SOL-GEL-DERIVED ANTI-REFLECTION OPTICAL COATINGS[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,1997(1/2):185-195. |
| [4] | Liu Y;Ren W;Zhang L Y et al.[J].Thin Solid Films,1999,353:124-128. |
| [5] | 贾巧英,乐月琴,唐永兴,姜中宏.溶胶-凝胶法制备耐磨宽带SiO2/TiO2增透膜[J].光学学报,2004(01):65-69. |
| [6] | Belleville P;Prené P;Lambert B .[J].Proceedings of SPIE,2000,3943:67-71. |
| [7] | 孙继红.SiO2光学增透膜的制备及光学性能[J].光学技术,2000(02):104-106. |
| [8] | 熊华山,陈宁,张清华,王克,殷勤俭,江波.Sol-gel制备SiO2增透膜的研究[J].功能材料,2004(04):485-486. |
| [9] | 付甜,吴广明,沈军,肖轶群,张志华,杨帆,王珏.溶胶-凝胶法制备宽带减反膜[J].功能材料,2003(05):579-581,584. |
| [10] | 樊先平,郝霄鹏,姚华文,王民权.TiO2-SiO2系统凝胶玻璃薄膜折射率的研究[J].功能材料,2002(02):215-217. |
| [11] | 潘祖仁.高分子化学[M].北京:化学工业出版社,2002 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%