The sputtered nanocrystalline coating of K38G alloy was obtained by magnetron sput-tering. The hot corrosion behaviors of cast K38G alloy and its sputtered nanocrys-talline coating by pre-deposited 75wt%Na2SO4+25wt%K2SO4 at 900℃ were studied.The results indicated the occurrence of internal sulfidation in the cast K38G alloy withpre-deposited sulfattes of 0.8 and 3.0mg/cm2. However, the internal sulfidation wasnot observed in the coating with pre-deposited 0. 8mg/cm2 sulfate. The hot corrosionresistance of K38G alloy was clearly enhanced through nanocrystallinzation, althoughthe internal sulfides were still formed for the coating with sulfate deposit of 3mg/cm2.The relevant hot corrosion mechanism was also discussed.
参考文献
| [1] | Fuhui Wang;H Y Lou;L X Bai .[J].Chin Journal of Met Science Technology,1990,6(06):61. |
| [2] | H Y Lou;Fuhui Wang .[J].Oxidation of Metals,1992(38):299. |
| [3] | Fuhui Wang .[J].Oxidation of Metals,1997(48):215. |
| [4] | Fuhui Wang;D J Young .[J].Oxidation of Metals,1997(48):497. |
| [5] | E Janecke;Z Physik .[J].Chemistry:a European Journal,1998(64):346. |
| [6] | A Goebel;F S Pettit;G W Goward .[J].Metallurgical and Materials Transactions,1973,4(04):261. |
| [7] | Y S Zhang .[J].Journal of the Electrochemical Society,1986(133):655. |
| [8] | S J Geng .[D].Shenyang:Institute of Metal Research,The Chinese Academy of Sciences.PhD Dissertation,2001. |
| [9] | M C Wang;Z J Jin .[J].Journal Chinese Society for Corrosion and Protection,1986,6:65. |
| [10] | Y S Zhang .[J].Journal Chinese Society for Corrosion and Protection,1989,9(09):121. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%