采用溶液共混法制备了不同质量比例的新型含二氮杂萘酮结构聚芳醚砜酮(PPESK)与聚四氟乙烯(PTFE)共混物.利用热失重(TGA)和动态热机械仪(DMTA)对该共混物的热性能和动态机械性能进行了表征和研究.结果表明:在PPESK中共混加入PTFE,提高了PPESK的起始分解温度及最大分解速率对应温度.该共混体系的损耗模量和损耗因子随着扫描频率的提高向高温转移,这是分子运动速率的提高所致.在30~230℃的扫描温度范围内,共混物的储能模量保持较高值并随着温度升高而降低趋势并不明显,耐热性能良好;但当扫描温度达到280℃后,接近其玻璃化转变温度时,储能模量降低幅度较大.在PPESK中共混加入10%PTFE可提高其玻璃化温度.
参考文献
[1] | D.R.Paul, S.Newman, Polymer blends Ⅰ and Ⅱ. (New York, Academic Press, 1977) p1 |
[2] | JIAN Xigao, Allans Hay, ZHENG Haibin, Preparation of Poly(phthalazinone ether sulfone)s, Chinese Patent:CN931091802, 1993-07-26(蹇锡高,Allans Hay,郑海斌.含二氮杂萘酮结构的聚醚砜及制备法,中国专利:CN931091802,1993-07-26) |
[3] | JIAN Xigao, Allans Hay, ZHENG Haibin. Preparation of poly (phthalazinone ether ketone)s [P]. Chinese Patent: CN931091799, 1993-07-26.(蹇锡高,Allans Hay,郑海斌.含二氮杂萘酮结构的聚醚酮及制备法,中国专利:CN931091799,1993-07-26) |
[4] | Guimei Wang, Xigao Jian, Gongxiong Liao, Lihao Wu, J. Mater. Sci., 20(5), 609(2004) |
[5] | M.Z.Meng, S.C.Tjong, A.S.Hay, Polymer, 39(10), 1845(1998) |
[6] | Gongxiong LIAO, Xigao JIAN, Jinyan WANG, J. Mater. Sci. Technol, 18(6), 561(2002) |
[7] | PENG Jing, JIAN Xigao, LIU Saoqiong, GUO Xiaoyuan, Chinese Journal of Materials Research, 15(2),244(2001)(彭静,蹇锡高,刘少琼,郭晓园,材料研究学报,15(2),244(2001)) |
[8] | Eric N. Browna, Dana M. Dattelbaumb, Polymer, 46(9), 3056(2005) |
[9] | ZHU Guiru, WANG Tonghua, ZHANG Shouhai, JIAN Xigao, CAI Tianxi, Journal of Dalian University of Technology, 44(1), 57(2004)(朱桂茹,王同华,张守海,蹇锡高,蔡天锡,大连理工大学学报,44(1),57(2004)) |
[10] | Stephen G. Kuzak, Arun Shanmugam, Journal of Applied Polymer Science, 73(5), 649(1999) |
[11] | M.J.Jenkins, Polymer, 41(18), 6803(2000) |
[12] | BIAN Meili, Dynamic Mechanical Thermal Analysis of Polymer and Composites, First version (Beijing,Chemical Industry Press, 2002) p.58(边梅丽,高聚物与复合材料的动态力学热分析,第一版(北京,化学工业出版社,2002)p.58) |
[13] | Bhanu Nandan, L.D.Kandpal, G.N.Mathur, Polymer, 44(4), 1267(2003) |
[14] | M.L.Lee, Y.Li, Y.P. Feng, C.W.Carter, Intermetallics, 10, 1061(2002) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%