三嵌段共聚物F127为模板剂,线性酚醛树脂为碳前驱体,采用溶剂挥发诱导有机-有机自组装法(EI-SA)制备了具有二维六方结构的有序介孔碳.利用FT-IR、XRD、TEM、N2吸附/脱附等方法对有序介孔碳的结构进行了表征,研究了不同焙烧温度和模板剂用量对有序介孔碳结构的影响.结果表明,当模板剂的用量一定时,有序介孔碳的孔径、孔容和孔壁厚度都随着焙烧温度的升高而降低,但比表面积却随着微孔含量的增加而增大.随着模板剂用量的增加,介孔碳的有序性降低.有序介孔碳PF-2-500的比表面积、孔径、孔容、孔壁厚度和微孔比表面积比分别为583.82m2/g、3.05nm、0.31cm3/g、3.40nm和361.18m2/g,而有序介孔碳PF-1-500的比表面积、孔径和孔容相对于PF-2-500有所提高,分别为647.79m2/g、3.44nm和0.41cm3/g,但微孔比表面积和孔壁厚度分别降低为309.46m2/g和3.35nm.
参考文献
| [1] | Dillon A C;Jones K M;Bekkedahl T A et al.Storage of hydrogen in single-walled carbon nanotubes[J].Nature,1997,386:377. |
| [2] | Wan, Y;Wang, HY;Zhao, QF;Klingstedt, M;Terasaki, O;Zhao, DY .Ordered Mesoporous Pd/Silica-Carbon as a Highly Active Heterogeneous Catalyst for Coupling Reaction of Chlorobenzene in Aqueous Media[J].Journal of the American Chemical Society,2009(12):4541-4550. |
| [3] | Xin Zhuang;Ying Wan;Cuimiao Feng .Highly Efficient Adsorption of Bulky Dye Molecules in Wastewater on Ordered Mesoporous Carbons[J].Chemistry of Materials: A Publication of the American Chemistry Society,2009(4):706-716. |
| [4] | Ruckenstein E.;Hu YH. .Catalytic preparation of narrow pore size distribution mesoporous carbon[J].Carbon: An International Journal Sponsored by the American Carbon Society,1998(3):269-275. |
| [5] | Gavalda S.;Thomson KT.;Gubbins KE.;Kaneko K. .Molecular modeling of carbon aerogels[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,2001(0):531-538. |
| [6] | Ozaki J;Endo N;Ohizumi W et al.Novel preparation method for the production of mesoporous carbon fiber from a polymer blend[J].Carbon,1997,35(07):1031. |
| [7] | Vinu, A;Srinivasu, P;Takahashi, M;Mori, T;Balasubramanian, VV;Ariga, K .Controlling the textural parameters of mesoporous carbon materials[J].Microporous and Mesoporous Materials,2007(1/3):20-26. |
| [8] | Yang, CM;Weidenthaler, C;Spliethoff, B;Mayanna, M;Schuth, F .Template synthesis of ordered mesoporous carbon with polypyrrole as carbon precursor[J].Chemistry of Materials,2005(2):355-358. |
| [9] | Tanaka S;Nishiyama N;Egashira Y et al.Synthesis of ordered mesoporous carbons with channel structure from an organic-organic nanocomposite[J].Chemical Communications,2005,16:2125. |
| [10] | Chengdu Liang;Kunlun Hong;Jimmy W.Ma .Synthesis of a Large-Scale Highly Ordered Porous Carbon Film by Self-Assembly of Block Copolymers[J].Angewandte Chemie,2004(43):5785-5789. |
| [11] | Matos JR.;Kruk M.;Mercuri LP.;Jaroniec M.;Zhao L.;Kamiyama T. Terasaki O.;Pinnavaia TJ.;Liu Y. .Ordered mesoporous silica with large cage-like pores: Structural identification and pore connectivity design by controlling the synthesis temperature and time[J].Journal of the American Chemical Society,2003(3):821-829. |
| [12] | Yan Meng;Dong Gu;Fuqiang Zhang;Yifeng Shi;Haifeng Yang;Zheng Li;Chengzhong Yu;Bo Tu;Dongyuan Zhao .Ordered Mesoporous Polymers and Homologous Carbon Frameworks:Amphiphilic Surfactant Templating and Direct Transformation[J].Angewandte Chemie,2005(43):7053-7059. |
| [13] | Meng Y;Gu D;Zhang FQ;Shi YF;Cheng L;Feng D;Wu ZX;Chen ZX;Wan Y;Stein A .A family of highly ordered mesoporous polymer resin and carbon structures from organic-organic self-assembly[J].Chemistry of Materials: A Publication of the American Chemistry Society,2006(18):4447-4464. |
| [14] | Zhang FQ;Gu D;Yu T;Zhang F;Xie SH;Zhang LJ;Deng YH;Wan Y;Tu B;Zhao DY .Mesoporous carbon single-crystals from organic-organic self-assembly[J].Journal of the American Chemical Society,2007(25):7746-7747. |
| [15] | Matos JR.;Kruk M.;Mercuri LP.;Jaroniec M.;Zhao L.;Kamiyama T. Terasaki O.;Pinnavaia TJ.;Liu Y. .Ordered mesoporous silica with large cage-like pores: Structural identification and pore connectivity design by controlling the synthesis temperature and time[J].Journal of the American Chemical Society,2003(3):821-829. |
| [16] | Neil B.McKeown;Peter M.Budd;Kadhum J.Msayib;Bader S.Ghanem;Helen J.Kingston;Carin E.Tattershall;Saad Makhseed;Kevin J.Reynolds;Detlev Fritsch .Polymers of Intrinsic Microporosity(PIMs):Bridging the Void between Microporous and Polymeric Materials[J].Chemistry: A European journal,2005(9):2611-2620. |
| [17] | Zhao D Y;Feng J L;Huo Q S et al.Triblock copolymer syntheses of mesoporous silica with periodic 50 to 300 angstrom pores[J].Science,1998,279(5350):548. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%