采用X射线衍射、磁性法和硬度测量等方法研究了深冷处理对高铬白口铸铁显微组织和硬化行为的影响.结果表明,去稳+深冷处理铸铁的硬度比未深冷处理铸铁明显提高,从HRC 64.1提高到HRC 67.0.这是因为深冷处理使高铬白口铸铁的残余奥氏体量大大下降,马氏体的大量形成和细微二次碳化物的析出强化作用显著提高了高铬白口铸铁的硬度.深冷处理后铸铁组织中仍存在少量残余奥氏体.
参考文献
| [1] | Tabrett C P;Sare I R .The Effect of Heat Treatment on the Abrasion Resistance of Alloy White Iron[J].Wear,1997,203-204:206-219. |
| [2] | Hann SK.;Gates JD. .A TRANSFORMATION TOUGHENING WHITE CAST IRON[J].Journal of Materials Science,1997(5):1249-1259. |
| [3] | Powell GLF.;Bee JV. .SECONDARY CARBIDE PRECIPITATION IN AN 18 WT-PERCENT CR-1 WT-PERCENT MO WHITE IRON[J].Journal of Materials Science,1996(3):707-711. |
| [4] | A. WIENGMOON;T. CHAIRUANGSRI;J. T. H. PEARCE .A Microstructural Study of Destabilised 30wt%Cr-2.3wt%C High Chromium Cast Iron[J].ISIJ International,2004(2):396-403. |
| [5] | C. P. Tabrett;I. R. Sare;M. R. Ghomashchi .Microstructure-property relationships in high chromium white iron alloys[J].International Materials Reviews,1996(2):59-82. |
| [6] | C. P. Tabrett;I. R. Sare .Effect of high temperature and sub-ambient treatments on the matrix structure and abrasion resistance of a high-chromium white iron[J].Scripta materialia,1998(12):1747-1753. |
| [7] | 何福善;尤华平;张茂勋.深冷处理在高络白口铸铁中的应用[J].机电技术,2003(z1):294-296. |
| [8] | J T H Pearce .High Chromium Cast Irons to Resist Abrasive Wear[J].Foundryman,2002(4):156-166. |
| [9] | 王均,孙志平,刘浩怀,高升吉,沈保罗,黄四九.一种高铬铸铁亚临界处理的硬化动力学研究[J].铸造,2003(11):1065-1068. |
| [10] | 周玉;武高辉.材料分析测试技术[M].哈尔滨:哈尔滨工业大学出版社,1998 |
| [11] | 徐祖耀.马氏体相边与马氏体[M].北京:科学出版社,1999 |
| [12] | 肖纪美.合金相与相变[M].北京:冶金工业出版社,2004 |
| [13] | 程本培,李勇,陈莉,任连治,李彩云.W6Mo5Cr4V2高速钢低温强化机理[J].科学通报,1995(16):1526-1530. |
| [14] | 李雄,李士燕,张鸿冰,阮雪榆.6W-5Mo-4Cr-2V高速钢深冷处理微观组织结构的分析[J].上海交通大学学报,2002(07):905-907,910. |
| [15] | Zhiping Sun;Rulin Zuo;Cong Li .TEM study on precipitation and transformation of secondary carbides in 16Cr-lMo-lCu white iron subjected to subcritical treatment[J].Materials Characterization,2004(5):403-409. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%