采用激光焊和TIG焊分别对TWIP钢进行焊接,通过显微组织观察、拉伸试验及显微硬度测试对比研究了两种焊接接头的组织和性能.结果表明:激光焊的焊缝中心为细小的等轴晶,靠近熔合线的组织多为柱状晶,几乎看不到热影响区；TIG焊的焊缝组织为取向基本一致的柱状晶且晶粒较大,热影响区为粗大的奥氏体组织；激光焊接头拉伸试样在远离焊缝的母材处断裂,抗拉强度为560 MPa,伸长率为67％,断口为典型的韧性断裂；TIG焊接头断裂在热影响区,抗拉强度为460 MPa,伸长率为48％,断口表现为脆性断裂,塑性变形能力明显低于激光焊接头的；激光焊接头的平均显微硬度高于TIG焊接接头的.
参考文献
| [1] | Grassel O.;Frommeyer G.;Meyer LW.;Kruger L. .High strength Fe-Mn-(Al, Si) TRIP/TWIP steels development - properties - application[J].International Journal of Plasticity,2000(10/11):1391-1409. |
| [2] | 李大赵,卫英慧,刘春月,侯利锋,刘东风,崖天燮,胡玉亭.汽车用TWIP钢的基础研究现状[J].钢铁研究学报,2009(02):1-5. |
| [3] | L. Mujica;S. Weber;H. Pinto;C. Thomy;F. Vollertsen .Microstructure and mechanical properties of laser-welded joints of TWIP and TRIP steels[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2010(7/8):2071-2078. |
| [4] | DING Hua,TANG Zheng-You,LI Wei,WANG Mei,SONG Dan.Microstructures and Mechanical Properties of Fe-Mn-(Al, Si) TRIP/TWIP Steels[J].钢铁研究学报（英文版）,2006(06):66-70. |
| [5] | Georg FROMMEYER;Udo BRUX;Peter NEUMANN .Supra-Ductile and High-Strength Manganese-TRIP/TWIP Steels for High Energy Absorption Purposes[J].ISIJ International,2003(3):438-446. |
| [6] | 严玲,唐荻,米振莉,郭锦.汽车用TWIP钢的力学性能与微观组织[J].北京科技大学学报,2006(08):739-743. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%