The maximum elongation-to-failure of 960% has been achieved in the Mg-8wt%Li alloy. It is shown by measurement of true stress-strain curve and microstructure observation that dynamic recrystallization takes place during superplastic deformation, which turns the banded grains into equiaxed grains. It is postulated by theoretical analysis that during superplastic deformation,continuous introduction of lattice dislocations into the phase interfaces contributes to the superplasticity in this alloy.During superplastic deformation,grain growth and cavity nucleation at α phase grain boundaries have also been observed.