采用原位粉末套管法(in-situ PIT)制备了MgB2/Fe线材.前驱粉末按照Mg∶B=1.1∶2的比例将Mg粉和B粉混合研磨,装入外径和内径分别为14×8mm、10×7mm和6×4mm的低碳钢管中,均拉拔至Φ1.18mm,然后800℃保温10min.通过扫描电子显微镜(SEM)和综合物性测试系统(PPMS)分析了样品的微观结构和超导电性.结果表明,MgB2超导线材粉芯填充因子主要由原始包套材料尺寸所决定,且在线材减径过程中变化微弱；微观结构显示,随着包套材料外径增加,芯部孔隙率减小,有效导电面积增加；同时,包套材料尺寸对线材临界电流也有影响,原始外径增大可提高临界电流密度.
参考文献
| [1] | Nagamatsu J;Nakagawa N;Muranaka T;Zenitani Y;Akimitsu J .Superconductivity at 39 K in magnesium diboride[J].Nature,2001(6824):63-64. |
| [2] | Shimura S;Machi T;Murakami M;Koshizuka N;Mochizuki K;Ishikawa I;Shibata N .Copper sheath MgB2 wires fabricated by an in situ PIT method[J].Physica, C. Superconductivity and its applications,2004(Pt.2):1179-1183. |
| [3] | Jiang CH;Nakane T;Hatakeyama H;Kumakura H .Enhanced J(c) property in nano-SiC doped thin MgB2/Fe wires by a modified in situ PIT process[J].Physica, C. Superconductivity and its applications,2005(3/4):127-131. |
| [4] | 刘国庆,王庆阳,孙昱艳,熊晓梅,焦高峰,闫果.热处理对C掺杂MgB2/Nb/Cu单芯线材微观结构及超导电性的影响[J].低温物理学报,2011(02):116-119. |
| [5] | 王小峰,李仪成,崔雅静,赵勇.葡萄糖掺杂对MgB2钉扎机制的影响[J].低温物理学报,2012(01):27-31. |
| [6] | 曹自林.粉芯钢管拉拔时的理论解析[J].机械工程与自动化,2007(03):64-67. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%